Method for gunning a refractory composition
AssigneeShinagawa Refractories Co., Ltd.
InventorsEiichi Yorita, Takashi Yamamura, Yukitoshi Kubota, Ichiro Hattori
Life of this patent
Estimating the term…
Abstract
The present invention was developed to solve the problems inherent in conventional dry type and wet type gunning methods. The main point of the present invention is a novel method for gunning a refractory composition for obtaining a lining body having high density and high strength by premixing a refractory composition with water amounting to 1/5-3/4 of the total amount of water for the lining, and subsequently adding and mixing the rest of the water at the inside of the gunning nozzle of the dry gunning equipment while gunning.
Claims11
A method for gunning a refractory composition composed of 93-60 wt. % refractory aggregate, 5-30 wt. % refractory super fine powder, 1-20 wt. % alumina cement and 0.01-0.5 wt. % (outer percentage) dispersion agent together with 0.01-2 wt. % (outer percentage) of a hardening accelerator characterized in that said refractory composition is first mixed with water amounting to 1/5-3/4 of the total amount used for the gunning, then conveyed under pressure by dry gunning equipment and then a solution containing the remaining amount of water and the hardening accelerator is added to said mixed refractory composition at a gunning nozzle of said dry gunning equipment wherein the total amount of water for the gunning is not more than 10% (outer percentage) of said refractory composition.
A method for gunning a refractory composition composed of 93-60 wt. % refractory aggregate, 5-30 wt. % refractory super fine powder, 1-20 wt. % alumina cement and 0.01-0.5 wt. % (outer percentage) of a dispersion agent together with 0.01-2 wt. % (outer percentage) of a hardening accelerator characterized in that said refractory composition is first mixed with water amounting to 1/5-3/4 of the total amount used for the gunning, then conveyed under pressure by dry gunning equipment and then a solution containing the remaining amount of water and the hardening accelerator is added to said mixed refractory composition at a gunning nozzle of said dry gunning equipment, wherein the total amount of water for the gunning is not more than 10% (outer percentage) of said refractory composition, said refractory aggregate being composed of one or more components selected from the group consisting of fired refractory clay, bauxite, sillimanite, mullite, alumina, silicon carbide, zircon, magnesia and chromite, said refractory super fine powder being composed of one or more components selected from the group consisting of clay, kaolinite, fine silica, fine alumina, fine zircon, fine magnesia and fine silicon carbide, said dispersion agent being composed of one or more components selected from the group consisting of alkali phosphates and alkali polyphosphates, said hardening accelerator being composed of one or more components selects from the group consisting of calcium hydroxide, sodium silicate and sodium aluminate and said alumina cement being composed of one or more components selected from the group consisting of hydraulic high alumina cement, and JIS (Japanese Industrial Standard) alumina cement No. 1 and No. 2.
Dependencies are inferred from the claim text.