Nickel-base superalloy systems
AssigneeGeneral Electric Company
InventorKeh-Minn Chang
Life of this patent
Estimating the term…
Abstract
Alloy compositions for nickel-base superalloys having the qualities of weldability, castability and forge-ability together with improved high temperature strength and rupture properties are disclosed. The weldability is improved by varying the Al, Ti, Nb and Ta content so as to insure that only the favorable .gamma." precipitates are formed in the alloy. The high temperature properties of the alloy compositions are optimized by controlling the content of the major alloying elements Co and Cr. Preferably the alloy is substantially free of Fe.
Claims10
A substantially iron-free nickel-base alloy consisting essentially of, in weight percent:
- about 12% to 24% chromium,
- about 5% to 20% cobalt;
- about 1% to 8.5% of at least one member of the group consisting of molybdenum, tungsten, and rhenium;
- about 2% to 23% tantalum;
- about 0.003% to 0.05% boron;
- less than about 1% iron;
- and the balance essentially nickel said alloy having a rupture life of at least 100 hours at a stress of 90 ksi at 1300 .degree. F. and a substantial volume fraction of gamma double prime phase.
A substantially iron-free nickel-base alloy consisting essentially of, in weight percent:
- about 12% to 24% chromium;
- about 5% to 20% cobalt;
- about 1% to 8.5% of a member of the group consisting of molybdenum, tungsten, and rhenium;
- about 2% to 23% tantalum;
- up to about 10.5% niobium;
- up to about 2.7% aluminum;
- up to about 3.7% titanium;
- about 0.003% to 0.05% boron;
- up to about 0.10% carbon;
- up to about 0.1% zirconium;
- up to about 1% iron;
- up to about 0.5% silicon;
- up to about 0.5% manganese;
- said alloy having a rupture life of at least 100 hours when subjected to a stress of 90 ksi at 1300.degree. F.
A nickel-base alloy of improved weldability consisting essentially, in weight percent, of:
- about 12% to 24% chromium;
- about 8% to 14% cobalt;
- about 1% to 8.5% of at least one member of the group consisting of molybedenum, tungsten, and rhenium;
- about 2.5% to 4.5% tantalum;
- about 0.003% to 0.05% boron;
- less than about 1% iron;
- up to about 10.5% niobium;
- up to about 2.7% aluminum;
- up to about 3.7% titanium;
- up to about 0.10% carbon;
- up to about 0.1% zirconium;
- up to about 0.5% silicon
- up to about 0.5% manganese;
- and the balance essentially nickel, said alloy having a rupture life of at leat 100 hours at a stress of 90 ksi at 1300.degree. F. and in the cast and heat treated condition a 0.2% yield strength of at least 115 ksi an ultimate tensile strength of at least 125 ksi at 1300.degree. F., and a substantial volume fraction of gamma double prime phase.
A substantially iron-free nickel-base alloy having improved weldability consisting essentially of, by weight percent:
- about 12% to 24% chromium;
- about 5% to 20% cobalt;
- about 1% to 8.5% of at least one member of the group consisting of molybdenum, tungsten and rhenium;
- up to about 1% iron;
- about 2% to 23% tantalum;
- about 0.003% to 0.05% boron;
- and the balance essentially nickel wherein the sum content, in atomic percent of aluminum plus titanium is from about 0.5 to about 3.0 and the sum content, in atomic percent, of niobium plus tantalum is from about 3.0 to about 7.5 and the value of the sum of the atomic percent of aluminum, titanium, niobium, and tantalum is from about 0.62 to about 0.95, and wherein said alloy in the forged and heat treated condition has a rupture life of at least 1800 hours when subjected to a stress of 120 ksi at 1200.degree. F.
A cast article of manufacture of a substantially iron-free nickel-base alloy consisting essentially of, in weight percent:
- about 12% to 24% chromium;
- about 5% to 20% cobalt;
- about 1% to 8% of a member of the group consisting of molybdenum, tungsten, and rhenium;
- about 2% to 23% tantalum;
- up to about 10.5 niobium;
- up to about 2.7% aluminum;
- up to about 3.7% titanium;
- about 0.003% to 0.05% boron;
- up to about 0.10% carbon;
- up to about 0.1% zirconium;
- up to about 1% iron;
- up to about 0.5% silicon;
- up to about 0.5% manganese;
- the balance being essentially nickel, said alloy having a rupture life of at least 100 hours when subjected to a stress of 90 ksi at 1300.degree. F., said article being characterized by the presence of a substantial volume fraction of gamma double prime phase.
Dependencies are inferred from the claim text.