Process for producing a semiconductor device having a silicon oxynitride insulative film

A process for producing a semiconductor device including at least one MISFET comprising the steps of:

• forming a silicon dioxide film on a semiconductor silicon substrate by thermal oxidation thereof;
• heating said silicon dioxide film in a plasma nitridation atmosphere to a temperature in the range of 800.degree. C. to 1300.degree. C.;
• replacing oxygen atoms of said silicon dioxide film with nitrogen of said nitridation atmosphere, while said nitrogen diffuses through said silicon dioxide film so as to form an insulative film by converting at least a surface portion of said silicon dioxide to at least silicon oxynitride at least at a surface portion of said silicon dioxide film and so that a distribution of nitrogen in the film decreases with the depth from the top portion toward the inside of the film;
• depositing a first film comprising one of a polycrystalline a silicon and metal silicide film on said insulative film;
• selectively removing said first film, thereby providing the remaining first film with a pattern of a gate electrode of said at least one MISFET element and exposing a portion of said insulative film;
• heating said semiconductor silicon substrate to form a silicon dioxide film on said first film and essentially converting said silicon oxynitride to silicon dioxide, said ioxide of said first film comprising a thickness substantially greater than said oxidized insulative film;
• and
• removing said exposed insulative film, to selectively expose said semiconductor silicon substrate, while the silicon dioxide film on said first film is removed by an amount corresponding to the thickness of said exposed insulative film being removed.

A method of forming an insulative film for multiple purposes in the field of semiconductor devices, said method comprising:

• providing a substrate of single crystal silicon;
• heating said substrate in an oxidizing atmosphere to oxidize a surface layer of said substrate;
• heating said substrate in a plasma nitridation atmoshpere to a temperature in the range of 800.degree. C. to 1300.degree. C.;
• replacing oxygen atoms of the silicon dioxide film with nitrogen of said nitridation atmosphere, while said nitrogen diffuses through the silicon dioxide film so as to at least partialy nitridate at least a surface portion of said oxide, and so that a distribution of nitrogen in the film decreases with the depth from the top portion toward the inside of the film.

A process for producing a semiconductor device including an insulative film comprising the steps of:

• forming a silicon dioxide film on the semiconductor device by thermal oxidation;
• heating said silicon dioxide film in a plasma nitridation atmosphere to a temperature in the range of 800.degree. C. to 1300.degree. C.;
• and
• replacing oxygen atom of said silicon dioxide film with nitrogen of said nitridation atmosphere, while said nitrogen diffuses through said silicon dioxide film so as to convert at least a surface portion of said silicon dioxide film to at least silicon oxynitride, and so that a distribution of nitrogen in the film decreases with the depth from the top portion toward the inside of the film.