Laser CVD and plasma CVD of CrO.sub.2 films and cobalt doped CrO.sub.2 films using organometallic precursors
AssigneeSyracuse University
InventorsPeter A. Dowben, Marshall Onellion
Life of this patent
Estimating the term…
Abstract
Chromium dioxide is deposited as a ferromagnetic layer onto selected portions of a substrate or over the entire substrate. Chromium hexacarbonyl vapor is introduced into a vacuum deposition chamber at e.g. 10 milliTorr and oxygen is introduced at e.g. 15 to 100 milliTorr. A UV laser beam is focused onto the substrate to form the CrO.sub.2 layer photolytically. The CrO.sub.2 layer can also be deposited by RF plasma deposition. This technique can also be employed for depositing MoC.sub.2, WC.sub.2, Mo.sub.2 .phi..sub.3, MoO.sub.2 or WO.sub.2. Magnetic recording or memory devices are produced without the high failure rate typical of the prior art sputtering technique.
Claims14
Process for depositing on a substrate a film of a magnetic oxide by decomposition of an organometallic precursor selected from the group consisting of Group VIB metal hexacarbonyls, chromacene and benzene chromium, the process comprising placing the substrate into a vacuum deposition chamber;
- introducing said organometallic precursor into said chamber as a vapor under a suitable pressure;
- introducing into the chamber an oxidizing agent as a vapor selected from the group consisting of O.sub.2 , O.sub.3 and NO under a suitable pressure greater than the pressure of said organometallic precursor vapor;
- maintaining the temperature of the substrate at a predetermined level to facilitate deposition onto a surface of said substrate;
- and applying UV or RF electromagnetic energy in said chamber to decompose the organometallic material and deposit the film of the magnetic oxide.
Process for depositing on a substrate a film of a metal oxide by laser-assisted chemical vapor deposition employing an organometallic precursor selected from the group that consists of Group VIB metal hexacarbonyls, chromacene, and benzene chromium the process comprising placing the substrate into a vacuum deposition chamber, introducing into the chamber said organometallic precursor as a vapor under suitable pressure;
- introducing into the chamber an oxidizing agent as a vapor under a suitable pressure greater than the pressure of said organometallic precursor vapor;
- maintaining the temperature of the substrate at a temperature below 350 K, and photolytically decomposing the organometallic precursor by focusing onto a predetermined portion of said substrate a laser beam whose wavelength is in the ultraviolet range, to produce said film on said predetermined portion of said substrate.
Process for depositing on a substrate a film of a Group VIB metal dioxide by decomposition of an organometallic precursor selected from type VIB metal hexacarbonyls, chromacene, and benzene chromium the process comprising placing the substrate into a plasma deposition chamber, introducing into the chamber said organometallic material as a vapor under a suitable pressure;
- introducing into said chamber an oxidizing agent as a vapor under a suitable pressure greater than the pressure of said organometallic precursor vapor;
- maintaining the temperature of the substrate at substantially 423-573 K and applying RF radiation to the chamber to create a plasma of said organometallic precursor vapor and said oxidizing agent vapor to decompose said organometallic precursor and form said Group VIB metal dioxide film on a surface of said substrate.