Selective deposition of amorphous and polycrystalline silicon
AssigneeMotorola, Inc.
InventorsHang M. Liaw, Christian A. Seelbach
Life of this patent
Estimating the term…
Abstract
A method for selectively depositing amorphous or polycrystalline silicon wherein a wafer having exposed silicon regions thereon is placed into a CVD reactor and subjected to a silicon containing gas and a halogen containing gas, at least one of which flows into the reactor with a hydrogen carrier gas. Amorphous silicon may be selectively deposited in the range of approximately 200 to 550 degrees centigrade while polycrystalline silicon may be selectively deposited in the range of approximately 550 to 750 degrees centigrade. It is also possible to deposit polycrystalline silicon at temperatures in the range of approximately 750 to 1000 degrees centigrade by employing another embodiment of the present invention.
Claims20
A method for selectively depositing amorphous or polycrystalline silicon comprising the steps of:
- placing a wafer having exposed silicon regions thereon into a CVD reactor;
- and
- subjecting said wafer to gas mixture consisting essentially of a silicon containing gas and a halogen containing gas, at least one of said gases flowing into said reactor with a hydrogen carrier gas.
A method for selectively depositing amorphous or polycrystalline silicon comprising the steps of:
- placing a wafer having exposed silicon regions thereon into a CVD reactor;
- heating said rector to a temperature in the range of approximately 200 to 550 degrees centigrade for the selective deposition of amorphous silicon or in the range of approximately 550 to 750 degrees centigrade for the selective deposition of polycrystalline silicon;
- and
- subjecting said wafer to a silane and a halogen containing gas, at least one of said gases flowing into said reactor with a hydrogen carrier gas.
A method for selectively depositing polycrystalline silicon comprising the steps of:
- placing a wafer having exposed silicon regions thereon into a CVD reactor;
- heating said reactor to a temperature in the range of approximately 750 to 1000 degrees centigrade;
- and
- subjecting said wafer to a gas including silicon and a halogen, said gas flowing into said reactor with a hydrogen carrier gas, said gas further having a higher halogen content initially for seeding and a lower halogen content following seeding for the remainder of the deposition.
A method for selectively depositing polycrystalline silicon comprising the steps of:
- placing a wafer having exposed silicon regions thereon into a CVD reactor;
- heating said reactor to a temperature of approximately 850 degrees centigrade and setting the reactor pressure at approximately 55 torr;
- subjecting said wafer to silicon tetrachloride gas flowing into said reactor with a hydrogen carrier gas at a hydrogen flow rate in the range of 15 to 32 liters/minute for approximately 5 minutes;
- and
- subjecting said wafer to a gas mixture of, dichlorosilane and hydrogen chloride.
A method for selectively depositing polycrystalline silicon comprising the steps of:
- placing a wafer having exposed silicon regions thereon into a CVD reactor;
- heating said reactor to a temperature in the range of approximately 750 to 1000 degrees centigrade;
- and
- subjecting said wafer to a gas including silicon and a halogen, said gas flowing into said reactor with a hydrogen carrier gas, said gas further maintaining the same composition throughout deposition and the initial seeding occurring at a lower temperature than the remainder of the deposition.
Dependencies are inferred from the claim text.