Composite breathable housewrap films
AssigneeExxon Chemical Patents Inc.
InventorParesh J. Sheth
Life of this patent
Estimating the term…
Abstract
Composite breathable film comprising a breathable polyolefin film heat laminated to a nonwoven HDPE fabric. Preferably, the breathable film is prepared by melt embossing a highly filled polyolefin film to impose a pattern of different film thickness therein, and stretching the embossed film. The nonwoven fabric is made by cross-laminating HDPE fibers at the crossing points to form a thin open mesh fabric, and coextruding a heat seal layer thereon. The composite is made by heat laminating the breathable film to the heat seal layer of the fabric. The resulting laminate has excellent water vapor transmissibility, air resistance and strength and is particularly adapted for use as a housewrap.
Claims17
A method of preparing a breathable laminate comprising a breathable polyolefin film having a water vapor transmission rate of at least about 3000 g/m.sup.2 per day and an air resistance not less than about 200 Gurley seconds and a fabric having an elongation less than about 30%, an Elmendorf tear strength of at least about 300 g, and a breakload of at least about 15 lb/in wherein said method comprises the step of laminating said film to said fabric at a temperature and pressure sufficient to bond the fabric and film.
A method of making a housewrap, comprising the steps of:
- mixing a polyolefin with a filler;
- extruding a precursor film from the polyolefin/filler mixture;
- melt embossing the precursor film to impose therein a pattern of different film thicknesses;
- stretching the melt embossed precursor film to impart greater permeability in the areas of reduced thickness thereof in comparison to the areas of greater thickness;
- and
- heat laminating the stretched film to a nonwoven fabric comprising cross-laminated fibers at a temperature and pressure sufficient to bond the fabric and film to form a breathable laminate.
A method of making a housewrap, comprising the steps of:
- mixing a polyolefin with a filler;
- cast extruding a precursor film of the polyolefin/filler mixture onto at least one melt embossing roller to impose therein a pattern of different film thicknesses;
- stretching the melt embossed precursor film in the transverse direction to impart greater permeability in the areas of reduced thickness thereof in comparison to the areas of greater thickness;
- heating a nonwoven fabric comprising cross-laminated polyolefin fibers and an ethylene-vinyl acetate copolymer heat seal layer;
- and
- pressing the heated fabric to the film at a temperature and pressure sufficient to bond the fabric and film to form a breathable laminate.