Method for fabricating buried waveguides
AssigneePolaroid Corporation
InventorAlfred R. Cooper
Life of this patent
Estimating the term…
Abstract
A method for fabricating buried waveguides on a glass substrate which contains sodium ions includes the steps of masking the substrate, performing a field-assisted ion-exchange process at low temperature to form waveguides by exchanging silver ions for the sodium ions, and performing a field-assisted ion-exchange at low temperature to bury the waveguides by exchanging potassium ions. In a preferred embodiment, the silver ions and the potassium ions are exchanged from eutectic melts.
Claims4
A method for fabricating buried waveguides in a multicomponent glass containing sodium ions, said method comprising the steps of:
- masking the surface of the substrate over the widthwise boundaries of the waveguide;
- placing the surface of the masked substrate in contact with a molten salt containing silver ions while maintaining the temperature of the substrate and salt below 250.degree. C.;
- applying an electric field across the substrate at a voltage within the range from 50 to a few hundred volts/mm to exchange silver ions in the molten salt for sodium ions in the glass substrate to raise the index or refraction of the unmasked region of the substrate depthwise to form the waveguide while minimizing the reduction of silver so that the absorption of the waveguide is lower than it would otherwise be if the temperature were above 250.degree. C.;
- immersing the masked substrate in a second molten salt containing a low index ion whose mobility is lower than that of the silver ion in the substrate glass while maintaining the substrate and second molten salt below a temperature of 250.degree. C.;
- and
- applying an electric field across the substrate to drive the silver ions further into the substrate while exchanging the low index ion for sodium to thereby bury the waveguide in the substrate to minimize scattering losses.
A method for fabricating, in a multicomponent glass substrate containing sodium ions, waveguides having sharp boundaries, said method comprising the steps of:
- depositing on the surface of the glass substrate at least two silver strips to facilitate defining the lateral extent of the waveguide;
- bringing the surface of the substrate with the silver strips into contact with a molten salt containing sodium;
- applying a potential difference to cause the simultaneous diffusion of silver and sodium ions with the silver ions from the silver strips entering the glass and being transported toward the opposite side of the substrate to form the high index region of the waveguide while elsewhere sodium ions from the salt are exchanged for sodium ions in the glass substrate thus providing the waveguide with sharply defined boundaries due to the nearly equal mobilities of sodium and silver;
- continuing to apply the electric field until the silver strips or consumed or until the integrated current reaches a predetermined value;
- removing any remaining silver metal from the substrate;
- and
- reapplying the electric field to drive the silver ions deeper into the substrate to bury the waveguide.