Flexible glass
OwnerDavid H. Blountinventor
Life of this patent
Estimating the term…
Abstract
Alkali metal silicate glass is mixed with water to form an aqueous alkali metal silicate glass suspension, then dried to form a flexible solid alkali metal silicate glass product which may be heated to above the boiling temperature of water to produce a cellular product. The flexible solid product may be utilized as a flexible film, as an adhesive, a coating agent and a binding agent. The foamed product may be used for thermal and sound insulation.
Claims10
A flexible alkali metal silicate glass-polymerized organic compound product produced by the following steps:
- (a) mixing 10 to 80 parts by weight of alkali metal glass having a SiO.sub.2 :alkali metal oxide ratio of 3.9:1 to 2.0:1 with 50 to 100 parts by weight of water until an aqueous alkali metal silicate glass suspension is produced;
- (b) admixing up to 300 percent by weight, based on weight of the aqueous alkali metal silicate glass suspension, of a polymerizable organic compound selected from the group consisting of vinyl monomers, diene monomers and mixtures thereof;
- (c) admixing and reacting up to 10 percent by weight, based on the weight of the aqueous alkali metal silicate glass suspension, of a free-radical initiator;
- (d) thereby producing an aqueous alkali metal silicate glass-polymerized organic compound suspension;
- (e) pouring or applying the aqueous alkali metal silicate glass-polymerized organic compound suspension into the desired form;
- (f) drying out water from the aqueous alkali metal silicate glass-polymerized organic compound suspension.
A flexible sodium silicate-polymerized vinyl monomer product produced by the following steps:
- (a) mixing 10 to 80 parts by weight of sodium silicate glass having a SiO.sub.2 :alkali metal oxide ratio of 3.9:1 to 2.0:1 with 50 to 100 parts by weight of water until an aqueous alkali metal silicate glass suspension is produced;
- (b) admixing up to 300 percent by weight, based on weight of the aqueous alkali metal silicate glass suspension, of a vinyl monomer;
- (c) admixing and reacting up to 10 percent by weight, based on the weight of the aqueous alkali metal silicate glass suspension, of a free-radical initiator;
- (d) thereby producing an aqueous sodium silicate glass-polymerized vinyl monomer suspension;
- (e) pouring or applying the aqueous sodium silicate glass-polymerized vinyl monomer suspension into the desired form;
- (f) drying out the water from the aqueous sodium silicate glass-polymerized vinyl monomer suspension.
A flexible sodium silicate-polymerized diene monomer product produced by the following steps:
- (a) mixing 10 to 80 parts by weight of sodium silicate glass having a SiO.sub.2 :alkali metal oxide ratio of 3.9:1 to 2.0:1 with 50 to 100 parts by weight of water until an aqueous alkali metal silicate glass suspension is produced;
- (b) admixing up to 300 percent by weight, based on weight of the aqueous alkali metal silicate glass suspension, of a diene monomer;
- (c) Admixing and reacting up to 10 percent by weight, based on the weight of the aqueous alkali metal silicate glass suspension, of a free-radical initiator;
- (d) thereby producing an aqueous sodium silicate glass-polymerized diene monomer suspension;
- (e) pouring or applying the aqueous sodium silicate glass-polymerized diene monomer suspension into the desired form;
- (f) drying the water from the aqueous sodium silicate glass-polymerized diene monomer suspension.
Aqueous alkali metal silicate glass-polymerized organic compound suspension produced by the process which consist of mixing and reacting the following components:
- (a) aqueous alkali metal silicate glass suspension containing 10 to 80 parts by weight of alkali metal silicate glass having a SiO.sub.2 :alkali metal oxide ratio of 3.9:1 to 2.0:1 in 50 to 100 parts by weight of water;
- (b) polymerizable organic compound selected from the group consisting of vinyl monomers, diene monomers and mixtures thereof, in the amount of up to 300 percent by weight, based on weight of the aqueous alkali metal silicate glass suspension;
- (c) free-radical initiator, in the amount of up to 10 percent by weight based on the weight of the aqueous alkali metal silicate glass suspension.
Dependencies are inferred from the claim text.