Molding of ceramic materials

A method for shaping a ceramic article by any of various ceramic shaping procedures which comprises the steps of (1) preparing a mold comprising a shaped porous, open-pore, hardened, plastic composition, said mold having been prepared from said composition by forming said composition from a water-in-oil emulsion comprising an aqueous phase dispersed in a continuous oil phase comprising (a) at least one unsaturated polyester resin dissolved in at least one hardenable compound containing at least one ethylenically unsaturated group and ((b) at least one emulsifying agent;

• incorporating in said water-in-oil emulsion about 2-12% by weight of said hardenable compound of a material effective in accelerating the formation of said ceramic article to be shaped in said mold, said material being selected from the group consisting of sodium disilicate a tetraborate;
• controlling the ratio of said aqueous phase to said oil phase of said emulsion so that said porous, open-pore, hardened, plastic composition has an open-pore volume, which is refillable with water, of about 10-60% of the total volume of said porous, open-pore, hardened, plastic composition;
• placing said water-in-oil emulsion into the desired mold shape;
• subjecting said hardenable compound of said continuous oil phase to hardening without breaking said water-in-oil emulsion of said composition, and then drying said shaped w to thereby obtain said mold of said shaped, porous, open-pore, hardened, plastic composition;
• (2) withdrawing water from said ceramic slip or ceramic plastic mass through said open pores of said mold to shape said ceramic article;
• (4) removing residual ceramic slip or ceramic plastic mass from said mold;
• (5) drying said resultant shaped ceramic article while in said mold;
• and (6) separating said dried ceramic article from said mold.