Preparation of physical blends of polymers and pigments
AssigneeDu Pont Canada Inc.
InventorPeter Y. Kelly
Life of this patent
Estimating the term…
Abstract
A method for the manufacture of a physical blend of pigment and a polymer powder whereby polymer powder having a particle size in the range of 250 to 750 microns is fed to a high intensity mixer and then powdered pigment is fed to the mixer at a rate of not more than 0.5 parts of pigment per 100 parts of polymer per minute. The pigment has a particle size that is substantially smaller than that of the polymer powder. The resultant admixture is mixed for a further period of time and then discharged from the mixer. The method is particularly applicable to powdered polyethylene intended for use in a rotational moulding process e.g. for the manufacture of containers and other hollow articles.
Claims13
A method for the manufacture of a physical blend of particles of polymer and pigment, said method comprising the steps of:
- (a) feeding a powder of a thermoplastic polymer to a high intensity mixer having a blade the spaced of at least 2,000 cm/sec, said powder having a particle size in the range of 250 to 750 microns;
- (b) feeding a powdered pigment to the high intensity mixer at a rate of not more than 0.5 parts of pigment per 100 parts of polymer powder per minute, said pigment being of a particle size that is not greater than 5% of the polymer, the polymer powder and pigment being admixed in said high intensity mixer during the period of addition of the pigment to the mixer;
- (c) subsequent to the feeding of the pigment to the mixer, continuing admixing of the polymer powder and pigment powder in the high intensity mixer for a period of time at least 50% as long as the time of addition of the pigment to the high intensity mixer;
- and
- (d) discharging the resultant physical blend of discrete particles from the mixer.
A process for the rotational moulding of articles, comprising:
- (a) feeding to the mould of rotational moulding apparatus a physical blend of particles of powdered polymer and pigment, said blend having been formed in a high intensity mixer by (i) feeding a powder of a thermoplastic polymer to a high intensity mixer having a blade speed of at least 2,000 cm/sec said powder having a particle size in the range of 250 to 750 microns, (ii) feeding a powdered pigment to the high intensity mixer at a rate of not more than 0.5 parts of pigment per 100 parts of polymer powder per minute, said pigment being of a particle size that is not greater than 5% of the polymer, the polymer powder and pigment being admixed in said high intensity mixer during the period of addition of the pigment to the mixer, (iii) subsequent to the feeding of the polymer to the mixer, continuing admixing of the polymer powder and pigment powder in the high intensity mixer for a period of time at least 50% as long as the time of addition of the pigment to the high intensity mixer, and (iv) discharging the resultant physical blend of discrete particles from the mixer;
- (b) rotating said mould about at least two axes while heating the mould, so that a molten layer of polymer containing pigment is formed on the inside of the mould;
- and
- (c) cooling the mould and removing the article so moulded.