Electrically conductive adhesive for a broad range of temperatures
AssigneesSiemens Aktiengesellschaft, Wacker Chemie AG
InventorsHanns-Heinz Peltz, Dietrich Wolfer
Life of this patent
Estimating the term…
Abstract
An electrically conductive adhesive having elasticity over a wide temperature range of approximately -60.degree. C. to about 180.degree. C. for securing sensitive electronic components to a foundation is provided.
Claims24
An electrically conductive adhesive for the planar joining of correspondingly planar parts to one another, the planar parts having mutually different temperature coefficients of the expansion of their materials, the adhesive being useful through a temperature range of approximately -60.degree. C. to about +180.degree. C., the adhesive is manufactured by the following steps:
- forming a composition that is cross-linkable to form an elastomer by the addition of organo polysiloxane with Si-bonded hydrogen (e), the composition comprising:
- (a) a di-organo polysiloxane with vinyl dimethyl siloxane units as end-position units, whereby the two Si-C-bonded organic radicals in the di-organo siloxane units are hydrocarbon radicals which are free from aliphatic multiple bonds;
- (b) silicon dioxide, employable as a filler, having a BET surface of approximately 100 to about 200 m.sup.2 g;
- (c) an organic solvent;
- and (d) a catalyst for promoting the agglomeration of Si-bonded hydrogen to vinyl groups, the di-organo polysiloxane (a) comprising approximately 10 to about 30 weight percent of the total composition that comprises constituents (a), (b), (c), and (d), the inorganic oxide (b) being present in the composition in a quantity of approximately 10 to about 40 weight percent with respect to the weight of the di-organo polysiloxane (a);
- stirring into the composition a sufficient amount of particle-shaped silver, chosen from the group consisting of dentritic silver, lamina-shaped silver, and spherical-shaped silver, so that the silver content is sufficiently great in the thickened condition of the resultant composition that the required electrical conductivity needed is present, the silver content, to afford the required electrical conductivity, comprises a minimum of 75% by weight of the resultant composition;
- after the particle-shaped silver is stirred into the composition, the resultant mixture containing the particle-shaped silver is thickened until a pasty working consistency is achieved and the solvent is eliminated;
- and
- mixing the resultant mixture obtained with organo polysiloxane (e) to effect cross-linking by heating the mixture, the organo polysiloxane (e) comprising approximately 1 to about 3 weight percent of the overall weight of the constituents (a) through (e) and of the silver constituent.
An electrically conductive adhesive for the planar joining of correspondingly planar parts to one another to create a component, the planar parts having mutually different temperature coefficients of the expansion of their materials, the adhesive being usable for components exposed to a temperature range of -60.degree. C. to about +180.degree. C., the adhesive being manufactured by:
- providing a composition that is cross-linkable to form an elastomer by the addition of organo polysiloxane with Si-bonded hydrogen (e), the composition comprising:
- (a) a di-organo polysiloxane with vinyl dimethyl siloxane units as end-position units, whereby the two Si-C-bonded organic radicals in the di-organo siloxane units are hydrocarbon radicals which are free from aliphatic multiple bonds;
- (b) an inorganic oxide filler having a BET surface of approximately 100 to about 200 m.sup.2 /g;
- (c) an organic solvent;
- and (d) a catalyst for promoting the agglomeration of Si-bonded hydrogen to vinyl groups, the di-organo polysiloxane (a) comprising approximately 10 to about 30 weight percent of the total composition that comprises constituents (a), (b), (c), and (d), the inorganic oxide (b) being present in the composition in a quantity of approximately 10 to about 40 weight percent with respect to the weight of the di-organo polysiloxane (a);
- stirring particle-shaped silver having a dentritic shape, lamina shape, or spherical shape into a composition, the amount of silver stirred into the composition being sufficient so that the silver content of the resultant adhesive is sufficiently great so that the required electrical conductivity needed is present, the silver content, to afford the required electrical conductivity, comprises a minimum of 75% by weight of the resultant adhesive;
- after the particle-shaped silver is added to the composition, the mixture is thickened until a pasty working consistency has been achieved;
- and
- the resultant mixture obtained in then mixed with an organo polysiloxane (e) having the formula:
- RSi(CH.sub.3).sub.2 O(SiR.sub.2 O).sub.p Si(CH.sub.3).sub.2 R
- wherein:
- R is hydrogen or the methyl, ethyl and/or phenyl radical, and only one hydrogen atom is bonded to a respective silicon atom, at least 0.2 Si-bonded hydrogen atoms are present on the average per silicon atom and at least three Si-bonded hydrogen atoms are present per molecule;
- and p is a whole number having a sufficient value so that the viscosity of these organo polysiloxanes (e) is approximately 4 to about 150mPa.s at 25.degree. C., the organo polysiloxane (e) comprising approximately 1 to about 3 weight percent of the overall weight of the constituents (a) through (e) and the silver constituent.
Dependencies are inferred from the claim text.