Aluminum alloy and master aluminum alloy for forming said improved alloy
AssigneeMetallurgical Products & Technologies, Inc.
InventorsDiran Apelain, Jung-Jen A. Cheng
Life of this patent
Estimating the term…
Abstract
An Al-Si base alloy to which is added predetermined amounts of Ti, preferably in the range from 0.2 to 1.0 weight percent Ti to significantly improve grain refinement and eutectic modification and to improve soundness and ductility of castings made of such an alloy, as well as reducing wear resistance of the casting. An Al-Ti or Al-Ti-B master alloy is utilized to produce the aforesaid alloy and is added to the melt to achieve the desired Ti level to produce a hypoeutectic and hypereutectic alloys. Alternatively, an Al-Ti-Si master alloy is added to the melt to obtain the desired Ti level for producing hypereutectic alloys.
Claims4
A master alloy for use in a hypereutectic casting alloy for improving grain refinement and eutectic modification consisting essentially of 76 to 88 weight percent aluminum;
- 8 to 4 weight percent titanium and 16 to 8 weight percent of silicon.
A metallic composition consisting essentially of a hypoeutectic aluminum-silicon alloy and titanium wherein the range of titanium is between 0.527 and 1.0 percent by weight.
A metallic composition consisting essentially of a hypoeutectic aluminum-silicon alloy and titanium in a range of from greater than 0.5 to 1.0 percent by weight;
- and
- further containing essentially 0.3 to 0.084 percent by weight of boron.
A hypereutectic casting aluminum-silicon alloy composition wherein grain refinement and eutectic modification is vastly improved through the addition of titanium to a hypereutectic aluminum-silicon casting alloy so that the resulting alloy consists essentially of a hypereutectic aluminum-silicon alloy wherein the range of titanium is between 0.527 and 1.0 percent by weight.