Heat treatment of exchangers to remove coke
AssigneeAshland Oil, Inc.
InventorJoe D. Turner
Life of this patent
Estimating the term…
Abstract
A method for removing furfural-derived coke from metallic surfaces by heating in an oxygen-containing gas, such as air, for a time and at a temperature sufficient to change the crush strength of the furfural coke to a point which will permit easy removal of such coke, without such an evolution of heat that the metallurgical properties of said metal surfaces are undesirably changed.
Claims12
A process for preparing furfural coke for removal from metallic surfaces comprising:
- heating said furfural coke without causing an evolution of heat capable of undesirably altering metallurgical properties of said surfaces in the presence of a gas containing molecular oxygen at a sufficient temperature below 800.degree. F. (427.degree. C.) for a sufficient time to change the crush strength of the coke so as to permit removal with a water jet at a pressure of five thousand pounds per square inch.
The process of claim one, wherein volatiles in said furfural coke are removed prior to said heating in the presence of molecular oxygen.
The process of claim two, wherein volatiles are removed by heating in an inert atmosphere.
The process of claim one, wherein said heating in the presence of molecular oxygen, is at a temperature in the range of about 400.degree. to 800.degree. F. (204.degree.-427.degree. C.).
The process of claim one, wherein said heating in the presence of molecular oxygen, is at a temperature in the range of about 550.degree. to 700.degree. F. (288.degree.-371.degree. C.).
The process of claim four, wherein said heating in the presence of molecular oxygen, is at a temperature in the range of about 550.degree. to 700.degree. F. (288.degree.-371.degree. C.).
The process of claim three, wherein said heating in the presence of molecular oxygen, is at a temperature in the range of about 550.degree. to 700.degree. F. (288.degree.-371.degree. C.).
A process for preparing furfural coke for removal from a metallic surface comprising:
- A. Removing volatiles without igniting them;
- B. Heating in the presence of molecular oxygen at a temperature and for a time sufficient to change the crush strength of the coke so as to permit easier removal of such coke than would otherwise be the case without damaging metallurgical properties of said metallic surface becauseof high evolution of heat.
The process of claim ten, wherein said heating is at a temperature in the range of about 400.degree. F. to 800.degree. F. (204.degree. C. to 427.degree. C.).