Method for electroplating nickel onto titanium alloys
AssigneeUnited Technologies Corporation
InventorsDonald E. Fornwalt, Gary M. Lomasney, Kostas Routsis
Life of this patent
Estimating the term…
Abstract
This invention relates to an improved method for electroplating a layer of nickel onto titanium base alloy substrates. It is particularly useful in electroplating a layer of nickel onto titanium alloys which contain refractory metal elements, such as the alloy Ti-8Al-1V-1Mo. The method includes the steps of etching the surface of the substrate with a solution containing hydrofluoric acid and hydrochloric acid, followed by electroplating the etched surface in a nickel sulfamate solution.
Claims4
A method for electroplating a layer of nickel onto a titanium base alloy containing refractory metal element, comprising the steps of etching the component surface in a solution having a composition corresponding to, by volume, about 4-6% of 70% HF and 94-96% of 36-38% HCl, and then cathodically plating a layer of nickel onto the etched surface.
A method for electroplating a layer of nickel onto the surface of a titanium base alloy component containing at least 1% by weight of a refractory metal element, comprising the steps of:
- (a) etching the component surface in a room temperature solution containing, by volume, about 94-96% of 36-38% HCl and about 4-6% of 70% HF for at least about 10 seconds;
- (b) anodically etching the component in a room temperature solution containing, by volume, about 11-15% of 70% HF, 81-85% glacial acetic acid and 2-6% H.sub.2 O;
- and
- (c) cathodically plating a layer of nickel onto the surface.
A method for applying a layer of nickel onto a titanium base alloy component containing at least 1 weight % of a refractory metal element, comprising the steps of:
- (a) etching the surface of the component in a room temperature solution consisting essentially of, by volume, about 94-96% of 36-38% HCl and about 4-6% of 70% HF for at least about 10 seconds;
- (b) anodically etching the component surface at about 1.4 amperes per square meter for about 6 minutes in a room temperature solution consisting essentially of, by volume, about 11-15% of 70% HF, 81-85% glacial acetic acid and 2-6% H.sub.2 O;
- and
- (c) cathodically plating a layer of nickel onto the etched component surface at 2.7 amperes per square meter for about 30 minutes in a nickel sulfamate solution.
Dependencies are inferred from the claim text.