Dielectric ceramic composition
AssigneeNippon Ferrite, Ltd.
InventorsTakashi Tsuboi, Hitoshi Ueda
Life of this patent
Estimating the term…
Abstract
A dielectric ceramic composition having a high relative dielectric constant a high quality factor and a small temperature coefficient of resonance frequency, consisting essentially of calcium oxide, strontium, oxide, bismuth oxide and titanium oxide, and having a composition represented by the formula: (CaO).sub.a.(SrO).sub.b.(Bi.sub.2 O.sub.3).sub.c.(TiO.sub.2).sub.d wherein 0.ltoreq.a<30, 0<b.ltoreq.20, 10.ltoreq.c.ltoreq.50, 40.ltoreq.d.ltoreq.80, and 0<a+b.ltoreq.30 by mol %. This composition may contain at least one of thallium oxide, yttrium oxide and manganese oxide and at least one of germanium oxide, zirconium oxide, tin oxide, cerium oxide and hafnium oxide.
Claims4
A dielectric ceramic composition consisting essentially of calcium oxide, strontium oxide, bismuth oxide and titanium oxide, and having a composition represented by the formula:
- (CaO).sub.a.(SrO).sub.b.(Bi.sub.2 O.sub.3).sub.c.(TiO.sub.2).sub.d
- wherein 0.ltoreq.a.ltoreq.10, 5.ltoreq.b.ltoreq.15, 25.ltoreq.c.ltoreq.30, 50.ltoreq.d.ltoreq.60, and 5.ltoreq.a+b.ltoreq.20 by mol %.
A dielectric ceramic composition consisting essentially of calcium oxide, strontium oxide, bismuth oxide, titanium oxide and at least one of germanium oxide, zirconium oxide, tin oxide, cerium oxide and hafnium oxide, and having a composition represented by the formula:
- (CaO).sub.a.(SrO).sub.b.(Bi.sub.2 O.sub.3).sub.c.(TiO.sub.2).sub.d.(RO.sub.2).sub.e
- wherein R represents at least one of Ge, Zr, Sn, Ce and Hf, and a, b, c, d and e satisfy 0.ltoreq.a.ltoreq.10, 5.ltoreq.b.ltoreq.15, 25.ltoreq.c.ltoreq.30, 50.ltoreq.c.ltoreq.60, 0.ltoreq.e.ltoreq.2 and 5.ltoreq.a+b.ltoreq.20 by mol %.
A sintered ceramic article consisting essentially of greater than 0 to less than 10 mol % CaO, greater than 5 to less than 15 mol % SrO, greater than 25 to less than 30 mol % Bi.sub.2 O.sub.3, greater than 50 to less than 60 mol % TiO.sub.2, the total content of CaO and SrO being greater than 5 but less than 20 mol %, said article having a quality factor under no load, Qo, of at least 100 and a temperature coefficient of resonance frequency, .tau.f, measured between -20.degree. C. and +60.degree. C. of .+-.100 ppm/.degree.C.
Dependencies are inferred from the claim text.