Control of form of crystal precipitation of aluminum hydroxide using cosolvents and varying caustic concentration
AssigneeBiotage AB
InventorRichard B. Wilhelmy
Life of this patent
Estimating the term…
Abstract
A process is disclosed for the control of the particle form of aluminum hydroxide crystals precipitated from an alkali metal aluminate solution which comprises either the use of certain monohydric and polyhydric alcohols or controlling the caustic concentration of the sodium aluminate solution or a combination whereby particles shapes may be produced principally comprising acicular form or principally comprising lamellar form, depending upon the caustic concentration of the alkali metal hydroxide and the vol. % of the alcohol.
Claims19
A process for the control of the crystal form of aluminum hydroxide crystals precipitated from a solution of alkali metal aluminate dissolved in an alkali metal hydroxide which comprises controlling the alkali metal hydroxide concentration of the alkali metal aluminate solution by preselecting an alkali metal hydroxide concentration in a range of from 0.1 to 6.5 molar, whereby crystal forms can be produced which range from principally comprising acicular to principally comprising lamellar form, depending upon said alkali metal hydroxide concentration, said crystals becoming more lamellar in shape when the caustic concentration is increased.
A process for the control of the crystal form of aluminum hydroxide crystals precipitated from an alkali metal aluminate solution which comprises selecting an alkali metal selected from the class consisting of sodium and potassium as the alkali metal in said alkali metal aluminate solution whereby crystal forms can be produced which range from principally comprising acicular to principally comprising lamellar form, with aluminum hydroxide crystals precipitated from potassium aluminate solutions being more acicular in habit than corresponding aluminum hydroxide crystals precipitated from sodium aluminate solutions.
A process for control of the crystal form of aluminum hydroxide crystals precipitated from an alkali metal aluminate solution which comprises:
- (a) selecting an alkali metal selected from the class consisting of sodium and potassium as the alkali metal in said alkali metal aluminate solution to influence the crystal form of said aluminum hydroxide crystals;
- and
- (b) adding to said solution from 1 to 50 vol.% of an alcohol selected from the class consisting of mono, di, and trihydric alcohols capable of influencing the crystal form of said aluminum hydroxide crystals without adversely effecting the yield of said crystals;
- whereby crystal forms can be produced which range from principally comprising acicular to principally comprising lamellar form, with aluminum hydroxide crystals precipitated from potassium aluminate solutions being more acicular in habit than corresponding aluminum hydroxide crystals precipitated from sodium aluminate solutions and the aluminum hydroxide crystals becoming more lamellar when the volume percent of the alcohol is increased in said alkali metal aluminate solution from which said crystals are precipitated.
A process for controlling the crystal form of an aluminum hydroxide crystal precipitated from an alkali metal aluminate solution which comprises:
- (a) forming an alkali metal aluminate solution by dissolving a sufficient amount of a source of aluminum in an alkali metal hydroxide selected from the class consisting of lithium hydroxide, sodium hydroxide, and potassium hydroxide to form an alkali metal aluminate solution having a (A1.sup.3+):
- (alkali metal hydroxide) molar ratio of from 0.6 to 0.8;
- (b) adjusting the alkali metal hydroxide concentration of said solution prior to precipitation of said aluminum hydroxide crystals therefrom to achieve a preselected diameter to length ratio of said aluminum hydroxide crystal in accordance with the formula:
- Log.sub.10 (Diameter/Length) =0.28 (MOH) -0.69
- wherein M = the alkali metal and (MOH) is the alkali metal hydroxide concentration in moles/dm.sup.3 ;
- (c) aging said solution at a temperature of from about 25 to 100.degree. C. for from 2 to 12 hours;
- and
- (d) precipitating aluminum hydroxide crystals having said preselected diameter to length ratio.
A process for controlling the crystal form of an aluminum hydroxide crystal precipitated from an alkali metal aluminate solution which comprises:
- (a) forming an alkali metal aluminate solution by dissolving a sufficient amount of a source of aluminum in an alkali metal hydroxide selected from the class consisting of lithium hydroxide, sodium hydroxide, and potassium hydroxide to form an alkali metal aluminate solution having a (A1.sup.3+):(alkali metal hydroxide) molar ratio of from 0.6 to 0.8;
- (b) adding to said solution from 1 to 50 vol.% of an alcohol selected from the class consisting of mono, di, and trihydric alcohols capable of influencing the crystal form of aluminum hydroxide crystals without adversely affecting the yield of said crystals;
- (c) adjusting the alkali metal hydroxide concentration of said solution and the amount of said alcohol in said solution prior to precipitation of said aluminum hydroxide crystals therefrom to achieve a preselected diameter to length ratio of said aluminum hydroxide crystals precipitated therefrom in accordance with the formula:
- Log.sub.10 (Axial Ratio) =0.28 (MOH) +0.036 (alcohol) -0.69
- wherein the Axial Ratio is the Diameter/Length ratio of the aluminum hydroxide crystal, M =alkali metal, (MOH) is the alkali metal hydroxide concentration in moles/dm.sup.3, and alcohol is the concentration of the alcohol in vol.%;
- (d) aging said solution at a temperature of from about 25.degree. to 100.degree. C. for from 2 to 12 hours;
- and
- (e) precipitating aluminum hydroxide crystals having said preselected diameter to length ratio.
Dependencies are inferred from the claim text.