US 4,880,759 AGranted

Ball clay slurry

AssigneeH. C. Spinks Clay Company Inc.

InventorWilliam Kohut

Life of this patent

Estimating the term…

Abstract

A ball clay/water slurry which may be used to prepare ceramic sanitaryware articles is disclosed. This slurry contains from 58 to 68 percent of ball clay with a specificed particle size distribution, 42 to 32 percent of water, 0.001 to 1.0 of organic polyelectrolyte, and from 50 to 650 parts per million of soluble sulfate ion. The slurry possesses rheological and casting rate properties which make it especially suitable for use in casting slips. It has a settling index of at least 0.9, a flow index of from 20 to 30 seconds, a casting rate of from 30 to 60 grams after 1 hour, and a transmission of at least 60 percent.

Claims20

Dependent claims

A ball clay/water slurry, wherein:

(a) said slurry is comprised of from about 58 to about 68 percent (by total weight of slurry) of ball clay (dry basis) and from about 42 to about 32 percent (by total weight of slurry) of water;
(b) said slurry has an initial Brookfield 100 rpm viscosity of from about 100 to about 600 centipoise;
(c) from about 30 to about 45 percent (by weight of dry ball clay) of the particles in said ball clay slurry are smaller than 0.5 microns, from about 53 to about 60 percent of the ball clay slurry particles are smaller than 2 microns, and from about 70 to about 85 percent of the ball clay slurry particles are smaller than 5 microns;
(d) said slurry has a specific surface area of from about 16 to about 21 square meters per gram;
(e) said slurry, when freshly made, has a five-minute gel viscosity at 0.5 revolutions per minute of from about 1,000 to about 10,000 centipoise;
(f) said slurry, when freshly made, has a ten-minute gel viscosity of from about 2,200 to about 12,000 centipoise;
(g) said slurry, when freshly made, has a twenty-minute gel viscosity of from about 3,500 to about 14,000 centipoise;
(h) the difference between the twenty-minute gel viscosity of the slurry and its ten-minute gel viscosity is less than about 3,000 centipoise;
(i) the difference between the twenty-minute gel viscosity of the slurry and its five minute gel viscosity is less than about 4,000 centipoise;
(j) the twenty-minute gel viscosity of a three-day old sample of said slurry is no more than 50 percent greater than the twenty-minute gel viscosity of the freshly-made slurry and is from about 3,500 to about 14,000 centipoise;
(k) said slurry contains from about 0.001 to about 1.0 percent of organic polyelectrolyte (weight of active ingredient, by weight of dry ball clay) wherein said organic polyelectrolyte has a molecular weight of from about 1,400 to about 6,000;
(1) said slurry contains from about 50 to about 650 parts per million (by weight of dry ball clay) of soluble sulfate ion;
(m) said slurry has a settling index of at least about 0.9;
(n) said slurry has a flow index of from about 20 to about 30 seconds;
(o) said slurry has a casting rate of from about 30 to about 60 grams after one hour;
(p) said slurry has a transmission of at least about 60 percent;
(q) said slurry has a dry modulus of from about 550 to about 700 pounds per square inch;
(r) said slurry contains from about 50 to about 65 percent (by weight of dry ball clay) of silica and from about 20 to about 35 percent of alumina;
(s) the silica/alumina weight ratio in said slurry is from about 2.0 to about 3.0;
and
(t) said slurry is comprised of from about 3 to about 20 percent (by weight of dry clay in the slurry) of mica, from about 6 to about 18 percent (by weight of dry clay in the slurry) of at least one montmorillonite mineral, from about 25 to about 70 percent (by weight of dry clay in the slurry) of at least one kaolinite mineral, and from about 7 to about 40 percent (by weight of dry clay in the slurry) of quartz.

18 more elements

Dependencies are inferred from the claim text.

patentgrep

Loading patent…

Abstract

A ball clay/water slurry, wherein:

(a) said slurry is comprised of from about 58 to about 68 percent (by total weight of slurry) of ball clay (dry basis) and from about 42 to about 32 percent (by total weight of slurry) of water;
(b) said slurry has an initial Brookfield 100 rpm viscosity of from about 100 to about 600 centipoise;
(c) from about 30 to about 45 percent (by weight of dry ball clay) of the particles in said ball clay slurry are smaller than 0.5 microns, from about 53 to about 60 percent of the ball clay slurry particles are smaller than 2 microns, and from about 70 to about 85 percent of the ball clay slurry particles are smaller than 5 microns;
(d) said slurry has a specific surface area of from about 16 to about 21 square meters per gram;
(e) said slurry, when freshly made, has a five-minute gel viscosity at 0.5 revolutions per minute of from about 1,000 to about 10,000 centipoise;
(f) said slurry, when freshly made, has a ten-minute gel viscosity of from about 2,200 to about 12,000 centipoise;
(g) said slurry, when freshly made, has a twenty-minute gel viscosity of from about 3,500 to about 14,000 centipoise;
(h) the difference between the twenty-minute gel viscosity of the slurry and its ten-minute gel viscosity is less than about 3,000 centipoise;
(i) the difference between the twenty-minute gel viscosity of the slurry and its five minute gel viscosity is less than about 4,000 centipoise;
(j) the twenty-minute gel viscosity of a three-day old sample of said slurry is no more than 50 percent greater than the twenty-minute gel viscosity of the freshly-made slurry and is from about 3,500 to about 14,000 centipoise;
(k) said slurry contains from about 0.001 to about 1.0 percent of organic polyelectrolyte (weight of active ingredient, by weight of dry ball clay) wherein said organic polyelectrolyte has a molecular weight of from about 1,400 to about 6,000;
(1) said slurry contains from about 50 to about 650 parts per million (by weight of dry ball clay) of soluble sulfate ion;
(m) said slurry has a settling index of at least about 0.9;
(n) said slurry has a flow index of from about 20 to about 30 seconds;
(o) said slurry has a casting rate of from about 30 to about 60 grams after one hour;
(p) said slurry has a transmission of at least about 60 percent;
(q) said slurry has a dry modulus of from about 550 to about 700 pounds per square inch;
(r) said slurry contains from about 50 to about 65 percent (by weight of dry ball clay) of silica and from about 20 to about 35 percent of alumina;
(s) the silica/alumina weight ratio in said slurry is from about 2.0 to about 3.0;
and
(t) said slurry is comprised of from about 3 to about 20 percent (by weight of dry clay in the slurry) of mica, from about 6 to about 18 percent (by weight of dry clay in the slurry) of at least one montmorillonite mineral, from about 25 to about 70 percent (by weight of dry clay in the slurry) of at least one kaolinite mineral, and from about 7 to about 40 percent (by weight of dry clay in the slurry) of quartz.

18 more elements