US 4,874,569 AGranted

Ceramic composite and methods of making the same

AssigneeLanxide Technology Company, LP

InventorsJack A. Kuszyk, Christopher R. Kennedy

Life of this patent

Estimating the term…

Loading patent…

Abstract

There is provided a method for producing a self-supporting ceramic composite comprising (1) a ceramic matrix obtained by oxidation of an aluminum zinc alloy to form a polycrystalline oxidation reaction product of the metal with an oxidant, and (2) one or more fillers embedded by the matrix. The metal alloy and permeable mass of filler having at least one defined surface boundary are oriented relative to each other so that formation of the oxidation reaction product will occur into said mass of filler and in a direction towards said defined surface boundary. On heating the metal to a first temperature above its melting point but below the melting point of said oxidation reaction product to form a body of molten parent metal, the molten metal reacts with said oxidant to form said oxidation reaction product which infiltrates said mass of filler to said defined surface boundary. The resulting infiltrated mass is heated to a second temperature in order to remove or oxidize at least a substantial portion of any residual non-oxidized metallic constituents from or in said infiltrated mass without substantial formation of said oxidation reaction product beyond said defined surface boundary, thereby producing a self-supporting ceramic composite.

Claims23

Dependent claims

A method for producing a self-supporting ceramic composite comprising (1) a ceramic matrix obtained by oxidation of a parent metal comprising an aluminum alloy to form a polycrystalline material comprising an oxidation reaction product of the parent metal with at least one oxidant;

and (2) at least one filler embedded by the matrix, which method comprises:
(a) positioning a parent metal, comprising an aluminum alloy having at least about 1% by weight zinc, adjacent to a permeable mass of filler having at least one defined surface boundary and orienting said parent metal and said filler relative to each other so that formation of an oxidation reaction product of the parent metal with an oxidant will occur into said mass of filler and in a direction towards said defined surface boundary;
(b) heating said parent metal to a first temperature above its melting point but below the melting point of said oxidation reaction product to form a body of molten parent metal and reacting the molten parent metal with said oxidant at said first temperature to form said oxidation reaction product, and at said first temperature maintaining at least a portion of said oxidation reaction product in contact with and extending between said body of molten metal and said oxidant, to draw molten metal through the oxidation reaction product towards the oxidant and towards and into the adjacent mass of filler so that fresh oxidation reaction product continues to form within the mass of filler at an interface between the oxidant and previously formed oxidation reaction product, and continuing said reaction for a time sufficient to infiltrate said mass of filler to said defined surface boundary, with said ceramic matrix, said ceramic matrix containing at least some residual non-oxidized metallic constituents of said parent metal;
and
(c) heating the resulting infiltrated mass of step (b) in at least one environment selected from the group consisting of an oxygen-containing atmosphere, an inert atmosphere and a vacuum to a second temperature above the first temperature but below the melting point of the oxidation reaction product to remove or oxidize at least a substantial portion of said residual non-oxidized metallic constituents of said parent metal without substantial formation of oxidation reaction product beyond said defined surface boundary, thereby producing a self-supporting ceramic composite.

2 more elements

and (2) at least one filler embedded by the matrix, which method comprises:
(a) positioning a parent metal, comprising an aluminum alloy having about 4-7% by weight zinc, adjacent to a permeable mass of filler having at least one defined surface boundary and orienting said parent metal and said filler relative to each other so that formation of an oxidation reaction product of the parent metal with an oxidant will occur into said mass of filler and in a direction towards said defined surface boundary;
(b) heating said parent metal to a first temperature above its melting point but below the melting point of said oxidation reaction product to form a body of molten parent metal and reacting the molten parent metal with said oxidant at said first temperature to form said oxidation reaction product, and at said first temperature maintaining at least a portion of said oxidation reaction product in contact with and extending between said body of molten metal and said oxidant, to draw molten metal through the oxidation reaction product towards the oxidant and towards and into the adjacent mass of filler so that fresh oxidation reaction product continues to form within the mass of filler at an interface between the oxidant and previously formed oxidation reaction product, and continuing said reaction for a time sufficient to infiltrate said mass of filler to said defined surface boundary, with said ceramic matrix, said ceramic matrix containing at least some residual non-oxidized metallic constituents of said parent metal;
and
(c) heating the resulting infiltrated mass of step (b) in at least one environment selected from the group consisting of an oxygen-containing atmosphere, an inert atmosphere and a vacuum to a second temperature above the first temperature but below the melting point of the oxidation reaction product to remove or oxidize at least a substantial portion of said residual non-oxidized metallic constituents of said parent metal without substantial formation of oxidation reaction product beyond said defined surface boundary, thereby producing a self-supporting ceramic composite.

2 more elements

Dependencies are inferred from the claim text.