Agglomerate absorbents comprising copper and zinc for sulphur compounds removal
AssigneeImperial Chemical Industries PLC
InventorsPatrick J. Denny, Peter Wood
Life of this patent
Estimating the term…
Abstract
Agglomerates containing oxides, hydroxides, carbonates and/or basic carbonates of copper, and zinc and/or another element such as aluminum or silicon, are useful for removal of sulphur compounds from fluids, especially under non-reducing conditions. The agglomerates have surface area above 80 m.sup.2.g.sup.-1 and a calcined density below 1.5 g.cm.sup.-3. After ignition, the cupric oxide plus zinc oxide (if any) content of the agglomerates is at least 70% w/w. The proportion of the copper compound is such that the copper atoms constitute 30-97% of the total of the copper, zinc, and said other element atoms in the agglomerates.
Claims8
Agglomerates capable of absorbing carbonyl sulphide, mercaptans, and hydrogen sulphide,
- said agglomerates having
- a size in the range 1 to 10 mm;
- a BET surface area of at least 80 m.sup.2 .multidot.g.sup.-1, measured on samples of the agglomerates that have been calcined for 4 hours at 350.degree. C.;
- a calcined density of not more than 1.5 g.multidot.cm.sup.-3 ;
- a porosity of not less than 0.6;
- and comprising
- (i) compounds of
- (a) copper, and
- (b) zinc and aluminum,
- said compounds being in the form of at least one compound selected from oxides, hydroxides, carbonates and/or basic carbonates;
- and
- (ii) calcium aluminate cement binder;
- said compounds being in such proportions that the copper atoms form 30-97% of the total number of copper, zinc, and aluminum atoms in said agglomerates;
- said agglomerates having a total copper and zinc compound content such that, after ignition at 900.degree. C., the cupric oxide plus zinc oxide content of the ignited composition is at least 70% by weight;
- and
- said binder constituting 5-10% by weight of said agglomerates.
Agglomerates capable of absorbing carbonyl sulphide, mercaptans, and hydrogen sulphide,
- said agglomerates having
- a size in the range 1 to 10 mm;
- a BET surface area of at least 80 m.sup.2 .multidot.g.sup.-1, measured on samples of the agglomerates that have been calcined for 4 hours at 350.degree. C.;
- a calcined density of not more than 1.5 g.multidot.cm.sup.-3 ;
- a porosity of not less than 0.6;
- and comprising
- (i) compounds of
- (a) copper, and
- (b) zinc and aluminum,
- said compounds being in the form of at least one compound selected from oxides, hydroxides, carbonates and/or basic carbonates;
- and
- (ii) a calcium aluminate cement binder;
- said compounds being in such proportions that the copper atoms form 30-97% of the total number of copper, zinc, and aluminum atoms in said agglomerates;
- and
- said agglomerates having a total copper and zinc compound content such that, after ignition at 900.degree. C., the cupric oxide plus zinc oxide content of the ignited composition is at least 80% by weight and said binder constitutes 5-10% by weight of said agglomerates.
Agglomerates capable of absorbing carbonyl sulphide, mercaptans, and hydrogen sulphide,
- said agglomerates having
- a size in the range 1 to 10 mm;
- a BET surface area of at least 80 m.sup.2 .multidot.g.sup.-1, measured on samples of the agglomerates that have been calcined for 4 hours at 350.degree. C.;
- a calcined density of not more than 1.5 g.multidot.cm.sup.-3 ;
- a porosity of not less than 0.6;
- and comprising
- (i) compounds of
- (a) copper, and
- (b) zinc and aluminum,
- said copper and zinc compounds being in the form of carbonates and/or basic carbonates;
- and said element aluminum being in the form of at least one compound selected from aluminum oxide of aluminum hydroxide;
- and
- (ii) a calcium aluminate cement binder;
- said compounds being in such proportions that the copper atoms form 30-97% of the total number of copper, zinc, and aluminum atoms in said agglomerates;
- and
- said agglomerates having a total copper and zinc compound content such that, after ignition at 900.degree. C., the cupric oxide plus zinc oxide content of the ignited composition is at least 70% by weight and said binder constitutes 5-10% by weight of said agglomerates.
A process for the manufacture of agglomerates capable of absorbing carbonyl sulphide, mercaptans, and hydrogen sulphide, having
- a size in the range 1 to 10 mm;
- a BET surface area of at least 80 m.sup.2 .multidot.g.sup.-1, measured on samples of the agglomerates that have been calcined for 4 hours at 350.degree. C.;
- a calcined density of not more than 1.5 g.multidot.cm.sup.-3 ;
- a porosity of not less than 0.6;
- said process comprising
- (i) precipitating compounds of
- (a) copper, and
- (b) zinc and aluminum,
- as hydroxides, carbonates and/or basic carbonates;
- (ii) mixing said compounds with a calcium aluminate cement binder;
- and
- (iii) agglomerating the resultant mixture to form said agglomerates;
- said compounds being in such proportions that the copper atoms from 30-97% of the total number of copper, zinc, and aluminum atoms in said agglomerates;
- and
- said agglomerates having a total copper and zinc compound content such that, after ignition at 90.degree. C., the cupric oxide plus zinc oxide content of the ignited composition is at least 70% by weight and said binder constitutes 5-10% by weight of said agglomerates.
Dependencies are inferred from the claim text.