Moldable silane-crosslinked polyolefin foam beads
AssigneeAstro-Valcour, Inc.
InventorsThomas M. Donuiff, Frederick H. Collins
Life of this patent
Estimating the term…
Abstract
Moldable foam beads comprising a silane-crosslinked polyolefin foam are produced by mixing a composition comprising a silane-modified polyolefin (such as a silane-grafted polyethylene) and a silanol condensation catalyst in an extruder to produce a melt, then injecting a blowing agent into the melt at a rate effective to produce a desired foam density in the extrudate; extruding and cutting the melt to form foam beads; and exposing the foam beads to moisture to produce silane crosslinking of the polyolefin foam.
Claims20
Moldable extrusion-foamed silane-crosslinked polyolefin foam beads.
Moldable foam beads comprising a silane-crosslinked polyolefin foam, produced by a process comprising the steps of:
- (a) mixing a composition comprising a silane-modified polyolefin and a silanol condensation catalyst in an extruder to produce a melt;
- (b) injecting a blowing agent into said melt at and rate effective to produce the desired foam density in the extrudate;
- (c) extruding and cutting said melt to foam said foams beads, and
- (d) exposing said foam beads to moisture to produce silane crosslinking of the polyolefin foam.
Moldable foam beads comprising a silane-crosslinked polyolefin foam, produced by a process comprising the steps of:
- (a) mixing a composition comprising a silane-modified polyolefin, a silanol condensation catalyst and a solid blowing agent in an extruder to produce a melt;
- (b) heating said melt to and temperature effective to activate said blowing agent;
- (c) maintaining the temperature of said melt at an acceptable foaming temperature at the die of said extruder;
- (d) extruder a cutting said melt to form said foam beads;
- and
- (e) exposing said foam beads to moisture to produce silane-crosslinking of the polyolefin foam.
Moldable foam beads formed of a silane-crosslinked polyolefin foam produced by a process comprising the steps of:
- (a) mixing a composition comprising a silane-grafted low density polyethylene and a silane condensation catalyst selected from the group consisting or organotin esters in an extruder to form a melt;
- (b) injecting a hydrocarbon or halogenated hydrocarbon blowing agent into said melt at a rate effective to cool said melt to foaming temperature and produce an extruded foam product having a density in the range of from about 1.5 to about 2.5 pcf;
- (c) extruding and cutting said melt to form said foam beads, and
- (d) exposing said foam beads to moist ambient air to produce substantially homogeneous silane crosslinking of the polyethylene foam.
Moldable silane-crosslinked polyolefin foam beads comprising low density or linear low density polyethylene, produced by extrusion foaming with a blowing agent selected from the group consisting a hydrocarbons and halogenated hydrocarbons, wherein said foam comprises a silanol condensation catalyst and the silane crosslinking is produced by exposure of said foam beads to moisture, the density of said foam thereafter being in the range of from about 1.2 to about 5 pcf and said foam being crosslinked to the extent that said beads are heat stable enough to be molded by application of heat and pressure.
Dependencies are inferred from the claim text.