Multilayered container and process for production thereof

A process for producing a biaxially oriented blow-molded container composed of a thermoplastic gas-barrier resin (resin B) and a thermoplastic resin (resin A) other than resin B and comprising

• a substantially non-oriented mouth portion composed of resin A, and
• the remainder consisting of (1) a portion composed of two layers of resin A and one layer of resin B which are laminated with the resin A layer and the resin B layer occurring alternately, (2) a portion composed of three layers of resin A and two layers of resin B which are laminated with the resin A layer and the resin B layer occurring alternately, and (3) a portion composed of two layers of resin A and one layer of resin B which are laminated with the resin A layer and the resin B layer occurring alternately, the portions (1), (2) and (3) extending in this order toward the bottom of the container;
• which comprises injecting resins A and B into a mold cavity to form a parison, and thereafter stretch blow-molding the parison, wherein the parison is formed by
• adjusting the total amount of resin B to be injected to 1 to 25% of the volume of the mold cavity, and
• (a) injecting resin A alone in an amount corresponding to 20 to 70% of the volume of the cavity,
• (b) simultaneously injecting resin B in an amount corresponding to 5 to 35% by weight of the total amount of resin B to be injected and resin A in an amount 1.0 to 10 times the amount of the resin B to be injected in this step,
• (c) injecting resin B in an amount corresponding to 30 to 90% of the total amount of resin B to be injected either alone or together with resin A in an amount not more than 2 times the amount of resin B to be injected in this step,
• (d) simultaneously injecting resin B in an amount corresponding to 5 to 35% of the total amount of resin B injected and resin A in an amount 1.0 to 10 times the amount of resin B to be injected in this step, and
• (e) finally injecting resin A alone in an amount corresponding to 10 to 70% of the volume of the cavity to fill the cavity.

A process for producing a biaxially oriented blow-molded container composed of a thermoplastic gas-barrier resin (resin B) and a thermoplastic resin (resin A) other than resin B and comprising

• a substantially non-oriented mouth portion composed of resin A, and
• the remainder consisting of (1) a portion composed of two layers of resin A and one layer of resin B which are laminated with the resin A layer and the resin B layer occurring alternately and (2) a portion composed of three layers of resin A and two layers of resin B which are laminated with the resin A layer and the resin B layer occurring alternately, the portions (1) and (2) extending in this order toward the bottom of the container;
• which comprises injecting resins A and B into a mold cavity to form a parison, and thereafter stretch blow-molding the parison, wherein the parison is formed by
• adjusting the total amount of resin B to be injected to 1 to 25% of the volume of the mold cavity, and
• (a) injecting resin A alone in an amount corresponding to 20 to 70% of the volume of the cavity,
• (b) simultaneously injecting resin B in an amount corresponding to 10 to 70% by weight of the total amount of resin B to be injected and resin A in an amount 1.0 to 10 times the amount of the resin B to be injected in this step,
• (c) injecting resin B in an amount corresponding to 30 to 90% of the total amount of resin B to be injected either alone or together wtih resin A in an amount not more than 2 times the amount of resin B to be injected in this step,
• (d) finally injecting resin A alone in an amount corresponding to 10 to 70% of the volume of the cavity to fill the cavity.

A process for producing a biaxially oriented blow-molded container composed of a thermoplastic gas-barrier resin (resin B) and a thermoplastic resin (resin A) other than resin B and comprising

• a substantially non-oriented mouth portion composed of resin A, and
• the remainder consisting of (1) a portion composed of three layers of resin A and two layers of resin B which are laminated with the resin A layer and the resin B layer occurring alternately, and (2) a portion composed of two layers of resin A and one layer of resin B which are laminated with the resin A layer and the resin B layer occurring alternately, the portions (1) and (2) extending in this order toward the bottom of the container;
• which comprises injecting resins A and B into a mold cavity to form a parison, and thereafter stretch blow-molding the parison. wherein the parison is formed by
• adjusting the total amount of resin B to be injected to 1 to 25% of the volume of the mold cavity, and
• (a) injecting resin A alone in an amount corresponding to 20 to 70% of the volume of the cavity,
• (b) injecting resin B in an amount corresponding to 30 to 90% of the total amount of resin B to be injected either alone or together with resin A in an amount not more than 2 times the amount of resin B to be injected in this step,
• (c) simultaneously injecting resin B in an amount corresponding to 10 to 70% of the total amount of resin B injected and resin A in an amount 1.0 to 10 times the amount of resin B to be injected in this step, and
• (d) finally injecting resin A alone in an amount corresponding to 10 to 70% of the volume of the cavity to fill the cavity.