Homogenous mixtures of polyphosphates
AssigneeOccidental Chemical Corporation
InventorsJohn A. Peterson, David C. Ehlers
Life of this patent
Estimating the term…
Abstract
A homogeneous, particulate mixture of alkali metal pyrophosphates and tripolyphosphates is prepared by flash drying an aqueous solution of alkali metal orthophosphates having an alkali metal to phosphorus mole ratio in the range of 5:3 to 6:3, and calcining the resultant dried particles. Preferably, the alkali metal is sodium and the orthophosphate solution is adjusted to provide a major proportion of sodium pyrophosphate and a minor proportion of sodium tripolyphosphate in the final product.
Claims1
A process for preparing a homogeneous, particulate mixture of tetrasodium pyrophosphate and trisodium orthophosphate, each of the phosphates being present in an amount of at least about 15% by weight of said mixture, said process consisting essentially of the steps of:
- (a) forming an aqueous solution of monosodium phosphate and disodium phosphate having a sodium to phosphorus mole ratio in the range of from 6:3 to 9:3,
- (b) flash drying the solution at a temperature in the range of from about 150.degree. C. to about 250.degree. C. to form phosphate particles,
- (c) calcining the dried particles at a temperature of from about 350.degree. C. to about 550.degree. C. to convert monosodium phosphate and disodium phosphate particles into said homogeneous, particulate mixture of tetrasodium pyrophosphate and trisodium orthophosphate, and
- (d) recovering a homogeneous mixture of tetrasodium pyrophosphate and trisodium orthophosphate particles of the
- desired fineness.