Method of manufacturing heat resistant, high-strength structural members of sintered aluminum alloy

Abstract

This invention relates to a method of manufacturing a structural member made of a sintered Al alloy having heat resistance and high strength. A powder is used having a composition which makes it difficult to perform hot forging, i.e. 8.0 to 30.0 wt. % of Si, 0.8 to 7.5 wt. % of Cu, 0.3 to 3.5 wt. % of Mg, 2.0 to 10.0 wt. % of Fe, 0.5 to 5.0 wt. % of Mn, and a balance of Al. After being subjected to press-forming, this Al alloy powder is subjected to hot extrusion at a temperature of 300.degree. to 450.degree. C., the extruded product is heated with electric resistance heating by electric current which is passed therethrough and subjected to forging at a temperature of 300.degree. to 495.degree. C. According to this method, a structural member made of a sintered Al alloy having heat resistance and high strength and having the aforementioned powder composition can be easily obtained without cracking.