Method for removing organic residue from as-synthesized zeolites
AssigneeMobil Oil Corporation
InventorFrancis X. Ryan
Life of this patent
Estimating the term…
Abstract
There is provided a three-step method for removing the residue of an organic directing agent from as-synthesized zeolites. The first step involves contacting the as-synthesized zeolite with an aqueous solution of a fluorosilicate salt such as ammonium fluorosilicate. The second step involves ion-exchanging the zeolite with an alkali metal or alkaline earth metal salt such as KCl. The third step involves calcining the ion-exchanged zeolite. This method is particularly useful for removing the residue of an organic directing agent from ZSM-18.
Claims2
A method for removing the residue of an organic directing agent from the as-synthesized form of ZSM-18, said organic directing agent being 1,3,4,6,7,9-hexahydro-2,2,5,5,8,8-hexmethyl-2H-benzo (1,2,-C:-3,4-C':5,6-C") tripyrolium trihydroxide, said method comprising the steps of:
- (i) contacting said as-synthesized form of ZSM-18 with an aqueous solution of ammonium fluorosilicate, said solution containing at least 0.0075 moles of said ammonium fluorosilicate per 100 grams of said as-synthesized ZSM-18;
- (ii) contacting said ammonium fluorosilicate contacted ZSM-18 of step (i) with a salt of potassium;
- (iii) calcining said ZSM-18 of step (ii) at a temperature of at least 250.degree. C. in an atmosphere containing NH.sub.3 ;
- and
- (iv) repeating said steps (i), (ii) and (iii) at least once.
A method for preparing the hydrogen form of ZSM-18 which is essentially free of residual organic directing agent, said method comprising the steps of:
- (i) forming an aqueous reaction mixture capable of forming ZSM-18, said reaction mixture comprising a directing agent which is 1,3,4,6,7,9-hexahydro-2,2,5,5,8,8-hexamethyl-2H-benzo (1,2,-C:-3,4,-C':5,6-C") tripyrolium trihydroxide, a source of sodium cations, a source of silica and a source of alumina, said reaction mixture having a composition, expressed in terms of mole ratios of T and oxides, as follows:
- SiO.sub.2 /Al.sub.2 O.sub.3 =5-30
- Na.sub.2 O/Al.sub.2 O.sub.3 =0.2-5
- H.sub.2 O/Al.sub.2 O.sub.3 =200-1500
- T/Al.sub.2 O.sub.3 =1-10
- where T is said directing agent;
- (ii) maintaining said reaction mixture of step (i) under conditions sufficient to form crystals of ZSM-18;
- (iii) separating said ZSM-18 crystals of step (ii) from the mother liquor of said reaction mixture by filtering said crystals and washing said crystals with water, whereby an as-synthesized form of ZSM-18 is obtained, said as-synthesized ZSM-18 having a residue of said organic directing agent in the pores of said ZSM-18;
- (iv) contacting said as-synthesized form of ZSM-18 of step (iii) with an aqueous solution of ammonium fluorosilicate, said solution containing at least 0.0075 moles of said ammonium fluorosilicate per 100 grams of said as-synthesized ZSM-18;
- (v) contacting said ammonium fluorosilicate contacted ZSM-18 of step (iv) with a salt of potassium;
- (vi) calcining said ZSM-18 of step (v) at a temperature of at least 250.degree. C. in an atmosphere containing NH.sub.3 ;
- (vii) repeating said steps (i), (ii) and (iii) at least once;
- (viii) contacting said ZSM-18 of step (vii) with an aqueous solution containing ammonium cations to obtain the ammonium exchanged form of ZSM-18;
- and
- (ix) calcining said ammonium form of ZSM-18 of step (viii) under conditions sufficient to evolve NH.sub.3 and to convert the ammonium form of ZSM-18 into the hydrogen form of ZSM-18.
Dependencies are inferred from the claim text.