Method for making a turbine blade having a wear resistant layer sintered to the blade tip surface

A method for applying a wear resistant layer to the tip surface of an article made of a high temperature metal alloy and having the shape of a gas turbine blade, the article also having a root portion and an airfoil portion, the layer characterized by a distribution of ceramic particulates in a high temperature metal alloy matrix, the method comprising the steps of removing plastic strain damage from the tip surface and airfoil surface of the article;

• disposing a mixture of ceramic particulates distributed within metal powder particles having said matrix alloy composition onto the tip surface of the article, the ceramic particulates being substantially nonreactive with the powder particles;
• heating the tip surface and said mixture thereon to a temperature sufficient to melt between about 50-90 percent of the powder particles and to cause the matrix and article alloys to diffuse with each other;
• thermally shielding the article airfoil portion and root portion, and removing heat from the article during said heating step;
• and then cooling the article to cause the melted powder particles to solidify.

A method of applying a wear resistant layer of material to the tip surface of a directionally solidified nickel base superalloy turbine blade, the blade also having a root portion and an airfoil portion, and having a columnar grain or single crystal microstructure characterized by gamma prime phase in a gamma phase matrix, the wear resistant layer characterized by aluminum oxide coated silicon carbide particulates distributed in a nickel base superalloy matrix having a different composition than said blade superalloy, the method comprising the steps of electropolishing the blade tip surface and airfoil surface to remove plastic strain damage therefrom;

• adhering a layer material to the tip surface of the blade, the layer material comprising thermoplastic resin, about 10-35 volume percent alumina coated silicon carbide particulates, and metal powder particles having said matrix composition;
• inductively heating the article to a first temperature range to volatilize the resin and then to a second temperature range to melt about 70-90% of the powder particles and to cause the matrix and blade alloys to melt and diffuse with each other;
• during said step of heating, thermally shielding the airfoil portion and root portion of the blade, and conductively transferring heat from the blade into a heat sink, such that recrystallization of the blade is prevented, and gamma prime phase growth is minimized;
• and cooling the blade to cause the melted powder particles to solidify.