Thermoplastic resin composition for cleaning
AssigneeChisso Corporation
InventorsHiroyuki Fujii, Takamichi Kudo, Haruhiko Furukawa, Nobusuke Yamamoto
Life of this patent
Estimating the term…
Abstract
A thermoplastic resin composition for cleaning a shaping apparatus such as an extrude by a simple operation, comprising 2-30% by weight of a sodium salt of sulfonic acid, 0.5-10% by weight of a water-repellent compound and a thermoplastic resin and as an optional component, finely ground inorganic compound having a particle size of 0.005 to 10 .mu.m.
Claims10
A thermoplastic resin composition for cleaning a shaping apparatus, comprising
- (1) 2-30% by weight of at least one sodium salt of sulfonic acid selected from the group consisting of sodium salt of alkylbenzenesulfonic acid having from 6 to 20 carbon atoms in alkyl group, sodium salt of alkylsulfonic acid having from 8 to 20 carbon atoms in alkyl group and sodium salt of diester of sulfosuccinic acid and alcohol having from 6 to 16 carbon atoms in alcohol residue,
- (2) 0.5-10% by weight of at least one water-repellent compound selected from the group consisting of metal salt of higher fatty acid, wax, liquid paraffin, synthetic wax and silicone, and
- (3) 60-97% by weight of a thermoplastic resin.
A thermoplastic resin composition for cleaning a shaping apparatus comprising
- (1) 2-30% by weight of at least one sodium salt of sulfonic acid selected from the group consisting of sodium salt of alkylbenzenesulfonic acid having from 6 to 20 carbon atoms in alkyl group, sodium salt of alkylsulfonic acid having from 8 to 20 carbon atoms in alkyl group and sodium salt of diester of sulfosuccinic acid and alcohol having from 6 to 16 carbon atoms in alcohol residue,
- (2) 0.5-10% by weight of at least one water-repellent compound selected from the group consisting of metal salt of higher fatty acid, wax, liquid paraffin, synthetic wax and silicone,
- (3) 0.05-5% by weight of at least one inorganic compound selected from the group consisting of silicon dioxide, white carbon, diatomaceous earth, calcium silicate, aluminum silicate, bentonite, zeolite, basic magnesium carbonate, natural gypsum, pumice and volcanic ash and having a particle size of from 0.005-10 .mu.m, and
- (4) 60-97% by weight of a thermoplastic resin.
A method for cleaning the interior of a shaping apparatus which contains residual amounts of a thermoplastic resin that has an undesirable color or odor which comprises introducing into the interior of said shaping apparatus and passing therethrough a cleaning composition that comprises
- (1) 2-30% by weight of at least one sodium salt of sulfonic acid selected from the group consisting of sodium salt of alkylbenzene sulfonic acid having from 6 to 20 carbon atoms in alkyl group, sodium salt of alkylsulfonic acid having from 8 to 20 carbon atoms in alkyl group and sodium salt of diester of sulfosuccinic acid and alcohol having from 6 to 16 carbon atoms in alcohol residue,
- (2) 0.5-10% by weight of at least one water-repellent compound selected from the group consisting of metal salt of higher fatty acid, wax, liquid paraffin, synthetic wax and silicone, and
- (3) 60-97% by weight of a thermoplastic resin.
A method for cleaning the interior of a shaping apparatus which contains residual amounts of a thermoplastic resin that has an undesirable color or odor which comprises introducing into the interior of said shaping apparatus and passing therethrough a cleaning composition that comprises
- (1) 2-30% by weight of at least one sodium salt of sulfonic acid selected from the group consisting of sodium salt of alkylbenzenesulfonic acid having from 6 to 20 carbon atoms in alkyl group, sodium salt of alkylsulfonic acid having from 8 to 20 carbon atoms in alkyl group and sodium salt of diester of sulfosuccinic acid and alcohol having from 6 to 16 carbon atoms in alcohol residue,
- (2) 0.5-10% by weight of at least one water-repellent compound selected from the group consisting of metal salt of higher fatty acid, wax, liquid paraffin, synthetic wax and silicone,
- (3) 0.05-5% by weight of at least one inorganic compound selected from the group consisting of silicone dioxide, white carbon, diatomaceous earth, calcium silicate, aluminum silicate, bentonite, zeolite, basic magnesium carbonate, natural gypsum, pumice and volcanic ash and having a particle size of from 0.005-10 .mu.m, and 60-97% by weight of a thermoplastic resin.
Dependencies are inferred from the claim text.