Composite silver base electrical contact material
AssigneeHamilton Standard Controls, Inc.
InventorNorman S. Bornstein
Life of this patent
Estimating the term…
Abstract
A silver base electrical contact material is described which contains a dispersion of particles consisting of cadmium oxide and nickel. The nickel particles are surrounded by a continuous adherent coating of nickel oxide which eliminates the detrimental reaction which would otherwise occur between nickel and cadmium oxide. The invention contact materials have improved lives and are fabricated by any one of several different powder metallurgy techniques.
Claims8
Method for producing electrical contact materials consisting of:
- compacting a blend of oxidized nickel powder and
- internally oxidized silver-cadmium powder wherein the resultant material contains 4 to 15 wt.% cadmium oxide, 2 to 8 wt.% oxidized nickel, balance essentially silver.
Method for producing electrical contact materials including the steps of:
- compacting silver powder, internally oxidized
- silver-cadmium powder and oxidized nickel powder wherein the resultant material contains 4 to 15 wt.% cadmium oxide, 2 to 8 wt.% oxidized nickel, balance essentially silver, and a portion of the silver is free from cadmium oxide particles.
Method for producing electrical contact materials including the steps of:
- (a) compacting a mixture of silver-cadmium alloy powder and oxidized nickel powder;
- (b) internally oxidizing the compact;
- wherein the resultant material contains 4 to 15 wt.% cadmium oxide, 2 to 8 wt.% oxidized nickel, balance essentially silver.
Method for producing electrical contact materials including the steps of:
- (a) compacting a mixture of silver powder, silver-cadmium alloy powder and oxidized nickel powder;
- (b) internally oxidizing the compact;
- wherein the resultant material contains 4 to 15 wt.% cadmium oxide, 2 to 8 wt.% oxidized nickel, balance essentially silver, and a portion of the silver is free from cadmium oxide particles.
Method for producing electrical contact materials including the steps of:
- (a) compacting a mixture of silver oxide powder, silver-cadmium alloy powder and oxidized nickel powder;
- (b) heating the compact to cause reduction of the silver oxide to silver and oxidation of the cadmium to cadmium oxide;
- wherein the resultant material contains 4 to 15 wt.% cadmium oxide, 2 to 8 wt.% oxidized nickel, balance essentially silver.
Method for producing electrical contact materials including the steps of:
- (a) compacting a mixture of silver powder, silver oxide powder, silver-cadmium alloy powder and oxidized nickel;
- (b) heating the compact to cause reduction of the silver oxide to silver and oxidation of the cadmium to cadmium oxide;
- wherein the resultant material contains 4 to 15 wt.% cadmium oxide, 2 to 8 wt.% oxidized nickel, balance essentially silver.
Method for producing electrical contact materials including the steps of:
- (a) compacting a mixture of cadmium oxide powder, silver powder and preoxidized nickel powder;
- wherein the resultant material contains 4 to 15 wt.% cadmium oxide, 2 to 8 wt.% oxidized nickel, balance essentially silver.
In the fabrication of silver-cadmium oxide contacts by powder metallurgy techniques, the improvement which comprises:
- adding from 2 to 8 wt.% of fine oxidized nickel powder prior to compaction.