Abstract
An early meltdown process of wax sweating is provided which enhances the efficiency, quality, product yield, and throughput of wax. In the early meltdown process, slack wax is crystallized. The crystallized wax is then sweated while simultaneously draining the liquid drippings from the sweating oven. The congealing point of the liquid drippings are monitored. When the congealing point of the liquid drippings indicate that the melting temperature of the desired wax product has been obtained, sweating and drainage are stopped, and the remaining solid bed of wax in the sweating oven is rapidly melted and subsequently upgraded.
Claims8
A wax sweating process, comprising the steps of:
- solidifying molten slack wax containing oil to crystallize said wax;
- sweating and substantially deoiling said wax to produce sweated wax by gradually and progressively heating said wax in a sweating oven to at least its melting point;
- while simultaneously
- withdrawing liquid drippings comprising some of said wax and oil from said sweating oven;
- graphing the wax sweating efficiency of said sweating oven on a nomograph with an abscissa comprising the congealing point of said liquid drippings and an ordinate comprising the ASTM melting point of said wax in said sweating oven;
- monitoring the congealing point of said liquid drippings as said solidified wax in said sweating oven is being heated by placing some of said liquid drippings on a thermometer, rotating said thermometer until said liquid drippings begin to congeal, and observing the congealing temperature of said liquid drippings on said thermometer;
- determining the ASTM melting point of the remaining solidified wax in said sweating oven by intersecting the monitored congealing temperature of said liquid drippings observed on said thermometer on said nomograph of said wax sweating efficiency of said sweating oven, drawing a horizontal line from said intersection to said ordinate of said nomograph, and observing said ASTM melting point on said ordinate;
- ceasing sweating and deoiling of the solidified wax in the sweating oven and withdrawal of said liquid drippings by closing the valves in said sweating oven when said determined ASTM melting point of said solidified wax in the sweating oven reaches the desired ASTM melting point of the desired wax product;
- thereafter
- heating said oven to melt the remaining solidified wax in the sweating oven without deoiling and separating liquid drippings from said wax to liquify and produce said desired wax product;
- discharging and draining said melted wax product from said sweating oven by opening said valves of said sweating oven;
- and
- collecting said melted wax product in a container selected from the group consisting of a pan, vessel, tank, bin, receptacle, pipe, drum, and kettle.
10 more elements
A wax sweating process, comprising the steps of:
- charging a sweating oven with a bed of sweatable molten slack wax containing oil to form a bed of slack wax;
- cooling said slack wax to a solidification temperature ranging from about 50.degree. F. to about 80.degree. F. to substantially solidify and crystallize said slack wax;
- progressively sweating said solidified wax by heating said bed of solidified wax at a rate ranging from about 0.5.degree. F./hr to about 2.degree. F./hr to at least the melting point of some of said wax to substantially deoil, fractionate, and partially liquify said wax;
- removing said partially liquified wax containing some of said oil from said sweating oven generally continuously during said sweating;
- periodically sampling said removed liquified wax and determining the oven drip congealing point of said sample liquified wax by placing some of said removed liquified wax on a thermometer, rotating said thermometer until said liquified wax begins to congeal, and observing the congealing temperature on said thermometer;
- monitoring and determining the ASTM melting point of the bed of solidified wax remaining in the sweating oven during said sweating on a nomograph of a plot of the liquified wax holdup in the sweating oven with an abscissa comprising the congealing point of said liquified wax and an ordinate comprising the ASTM melting point of said solidified wax in said sweating oven by linearly intersecting the observed congealing temperature on said thermometer with the plot of the liquified wax holdup of said sweating oven on said nomograph, drawing a horizontal line from said intersection to said ordinate on said nomograph, and oberserving the ASTM melting point of said solidified wax on said ordinate;
- ceasing removing said partially liquified wax and simultaneously stopping said deoiling and sweating of said bed of solidified wax in said sweating oven by closing the liquified wax rundown valve of said sweating oven upon monitoring and reaching the desired ASTM melting point of the bed of solidified wax remaining in said sweating oven;
- melting the bed of solidified wax after closing said liquified wax rundown valve by injecting steam into said sweating oven to substantially liquify all of the remaining wax in said sweating oven;
- draining said melted wax into wax retention pans;
- and
- hydrofinishing said melted wax by contacting said melted wax with hydrogen at a pressure ranging from about 140 psia to about 3675 psia and at a hydrogenation temperature ranging from about 400.degree. F. to about 755.degree. F. in the presence of a hydrogenation catalyst to produce the desired wax product.