Aggregate stabilization
OwnerRichard M. Burchinventor
Life of this patent
Estimating the term…
Abstract
The invention relates to an aggregate stabilizing emulsion comprising pitch, rosin, an emulsifying agent and water. The invention further relates to a method of stabilizing aggregate including a material produced from the aggregate which is pliable, weight supporting, freeze resistant, water impermeable and repairable and useful for paving, patching or sealing roadways, driveways and the like.
Claims22
A mixture for use as the dispersed phase in a stable, water dilutable, non-flammable, non-corrosive, dispersable, aggregate stabilizing emulsion consisting essentially of pine tar pitch from about 70 to about 90 weight percent based on the total weight of the mixture and rosin from about 1.0 to about 30 weight percent based on the total weight of the mixture wherein said mixture when emulsified with an emulsifying agent and water sufficiently to reduce the particle size of both the pine tar pitch and rosin to a maximum particle size of from about 5 to about 10 microns forms said aggregate stabilizing emulsion.
A stable, water dilutable, non-flammable, non-corrosive, dispersable, aggregate stabilizing emulsion consisting essentially of
- (a) from about 1 to about 90 weight percent based upon the total weight of said emulsion of a mixture comprising from about 5 to about 95 weight percent based upon the total weight of said mixture of pine tar pitch dispersed in said emulsion in a maximum particle size from about 5.0 to about 10.0 microns, and from about 1.0 to about 70.0 weight percent based upon the total weight of said mixture of a rosin dispersed in said emulsion in a maximum particle size from about 5.0 to about 10.0 microns,
- (b) from about 0.1 to about 5.0 weight percent based upon the total weight of said emulsion of a nonionic emulsifying agent, and
- (c) from about 10.0 to about 98.0 weight percent based upon the total weight of the emulsion of water.
A process for the stabilization of aggregate comprising:
- (a) first providing a stable emulsion comprising from about 1.0 to about 90.0 weight percent based upon the total weight of said emulsion of a mixture comprising from about 5.0 to about 95.0 weight percent based upon the total weight of said mixture of pine tar pitch dispersed in said emulsion with a maximum particle size of from about 5.0 to about 10.0 microns and from about 1.0 to about 70.0 weight percent based upon the total weight of said mixture of a rosin dispersed in said emulsion with a maximum particle size of from about 5.0 to about 10.0 microns, from about 0.1 to about 5.0 weight percent based upon the total weight of said emulsion of a nonionic emulsifying agent, and from about 10.0 to about 98.0 weight percent based upon the total weight of said emulsion of water,
- (b) secondly, providing an aggregate of a size which 100 weight percent based on the total weight of the aggregate passes through a sieve size from about number 200 to about one half inch,
- (c) thirdly mixing said aggregate with from about 2.0 to about 3.5 weight percent based upon the total weight of said aggregate of water,
- (d) forthly, mixing said emulsion with said pre-wet aggregate sufficiently to substantially disperse all of said diluted emulsion onto substantially all of said pre-wet aggregate, and
- (e) fifthly, compacting said aggregate with from about 50 pounds to about 50,000 pounds per square inch of compacting pressure resulting in said aggregate bonding together sufficiently after said water has substantially evaporated forming a strong, weight supporting, water impermeable, freeze resistant, solid material.
A stable, material consisting essentially of
- (a) an "(aggregate)" of a size which 100 weight percent based upon the total weight of said aggregate passes through a sieve size from about number 200 to about one half inch, said aggregate having dispersed thereon an emulsion comprising from about 5.0 to about 95.0 weight percent based upon the total weight of said emulsion of wood pine of pitch dispersed in said emulsion in a maximum particle size from about 5.0 to about 10.0 microns, and from about 1.0 to 70.0 weight percent based upon the total weight of said emulsion of a rosin dispersed in said emulsion in a maximum particle size from about 5.0 to about 10.0 microns, and
- (b) said "(aggregate)" coated with said emulsion having been compressed with from about 50 pounds to about 50,000 pounds per square inch forming a stable, weight supporting, freeze resistant, water impermeable, repairable, solid material.
A dispersed phase consisting essentially of pine tar pitch from about 70 to about 90 weight percent based on the total weight of the dispersed phase with a maximum particle size of from about 5 to about 10 microns and rosin from about 1.0 to about 30 weight percent based on the total weight of the dispersed phase with a maximum particle size of from about 5 to about 10 microns.