Polyester vessel and package
AssigneeToyo Seikan Kaisha, Ltd.
InventorsSadao Hirata, Yoshihiko Watanabe
Life of this patent
Estimating the term…
Abstract
Disclosed is a polyester vessel having mouth, side wall and bottom portions formed of a polyester composed mainly of ethylene terephthalate units, wherein the thermoplastic polyester is a polyester containing a catalyst residue in an amount smaller than 1000 ppm as the metal, and in the thermoplastic polyester constituting the bottom portion of the vessel, the ratio of the thermal crystallization degree represented by the following formula: 100.times.(Q.sub.DC -Q.sub.AC)/Q.sub.DC (1) wherein Q.sub.AC stands for the heat quantity of crystallization at elevation of the temperature and Q.sub.DC stands for the heat quantity of crystallization at lowering of the temperature, is lower than 90%.
Claims10
In a polyester vessel having mouth, side wall and bottom portions formed of a polyester composed mainly of ethylene terephthalate units, the improvement wherein said polyester is a thermoplastic polyester containing (i) a catalyst residue comprising Ge or Ti in an amount smaller than 1000 ppm as the metal and (ii) a phosphoric acid type stabilizer in an amount larger than 15 ppm as P in the case of the Ge-catalyst or in an amount larger than 55 ppm as P in the case of the Ti-catalyst, the upper limit of the amount of the phosphoric acid type stabilizer being smaller than 500 ppm as P, and in the thermoplastic polyester constituting the bottom portion of the vessel, the ratio of the thermal crystallization degree (V) represented by the following formula:
- V=100.times.(Q.sub.DC -Q.sub.AC)/Q.sub.DC ( 1)
- wherein Q.sub.AC stands for the heat quantity of crystallization at elevation of the temperature and Q.sub.DC stands for the heat quantity of crystallization at lowering of the temperature, is lower than 90%.
In a polyester package comprising a polyester vessel having mouth, side wall and bottom portions formed of a thermoplastic polyester composed mainly of ethylene terephthalate units and an edible oil filled and sealed in the polyester vessel, the improvement wherein said polyester is a thermoplastic polyester containing (i) a catalyst residue comprising Ge or Ti in an amount smaller than 1000 ppm as the metal and (ii) a phosphoric acid type stabilizer in an amount larger than 15 ppm as P in the case of the Ge-catalyst or in an amount larger than 55 ppm as P in the case of the Ti-catalyst, the upper limit of the amount of the phosphoric acid type stabilizer being smaller than 500 ppm as P, and in the thermoplastic polyester constituting the bottom portion of the vessel, the ratio of the thermal crystallization degree (V) represented by the following formula:
- V=100.times.(Q.sub.DC -Q.sub.AC)/Q.sub.DC ( 1)
- wherein Q.sub.AC stands for the heat quantity of crystallization at elevation of the temperature and Q.sub.DC stands for the heat quantity of crystallization at lowering of the temperature, is lower than 90%.
In a polyester vessel having mouth, side wall and bottom portions formed of a polyester composed mainly of ethylene terephthalate units, the improvement wherein said polyester is a thermoplastic polyester containing (i) a catalyst residue comprising Ge, Ti or Sb in an amount smaller than 1000 ppm as the metal and (ii) a phosphoric acid type stabilizer in an amount larger than 15 ppm as P in case of the Ge-catalyst, in an amount larger than 55 ppm as P in the case of the Ti-catalyst, or in an amount larger than 95 ppm as P in the case of the Sb-catalyst, the upper limit of the amount of the phosphoric acid type stabilizer being smaller than 500 ppm as P;
- in the thermoplastic polyester constituting the bottom portion of the vessel, the ratio of the thermal crystallization degree (V) represented by the following formula:
- V=100.times.(Q.sub.DC -Q.sub.AC)/Q.sub.DC ( 1)
- wherein Q.sub.AC stands for the heat quantity of crystallization at elevation of the temperature and Q.sub.DC stands for the heat quantity of crystallization at lowering of the temperature, is lower than 90%;
- and the bottom portion has a higher concentration of the phosphoric acid type stabilizer than the phosphoric acid type stabilizer concentration in the side wall portion.
Dependencies are inferred from the claim text.