US 4,816,233 AGranted

Ion exchange method for the recovery of scandium

AssigneeGTE Laboratories Incorporated

InventorsWilliam J. Rourke, Wen-Chao Lai, Samuel Natansohn

Life of this patent

Estimating the term…

Loading patent…

Abstract

A method of recovering quantitatively trace amounts of scandium from aqueous solutions containing large amounts of other metals consists of reducing any manganese and iron in the solution to the divalent states of manganese and iron. The solution is then adjusted to a pH from about 1.9 to about 2.1 and passed through a column of the ion exchange resin in the hydrogen form having an iminodiacetic acid functionality. The scandium is absorbed on the column and any base metals and rare earth metals which were also absorbed are removed by eluting with a dilute acid without removing the scandium. The scandium is subsequently removed from the column by eluting with a solution containing a chelating agent such as diglycolic acid. The scandium is then recovered from the solution by precipitation, filtering, washing, drying and calcined to the oxide.

Claims25

Dependent claims

A method of recovering scandium values from a tungsten ore residue comprising the following steps:

Step 1 dissolving scandium contained in a tungsten ore residue comprising iron, manganese, and scandium with an acid solution containing a reducing agent to convert any dissolved tetravalent manganese to divalent manganese forming an acid solution comprising said scandium, iron, and divalent manganese;
Step 2 converting any trivalent iron present in said acid solution comprising said scandium, iron, and divalent manganese from step 1 to divalent iron by adding an iron reducing agent forming a trivalent iron free acid solution comprising said scandium, divalent iron, and divalent manganese;
Step 3 adjusting said trivalent iron free solution comprising said scandium, divalent iron, and divalent manganese from step 2 to a pH from about 1.9 to about 2.1 to form a pH adjusted solution comprising said scandium, divalent iron, and divalent manganese;
Step 4 removing said scandium contained in said pH adjusted solution comprising said scandium, divalent iron, and divalent manganese from step 3 by contacting said pH adjusted solution comprising said scandium, divalent iron, and divalent manganese with an ion exchange resin being in a hydrogen form and having an iminodiacetic acid functionality forming an ion exchange resin having said scandium absorbed thereon;
Step 5 rinsing said ion exchange resin having said scandium absorbed thereon from step 4 with a dilute acid having a pH from about 1.9 to about 2.1 to remove any base metals and rare earth metals absorbed on said ion exchange resin without removing said scandium absorbed thereon;
Step 6 eluting said scandium absorbed on said ion exchange resin with a solution comprising a chelating agent to form an elution solution comprising said scandium and said chelating agent;
Step 7 precipitating said scandium from said elution solution comprising said scandium by adding a precipitating agent to said elution solution comprising said scandium to form a scandium precipitate in said elution solution;
and
Step 8 separating said scandium precipitate from said elution solution.

6 more elements

A method of recovering scandium from an aqueous solution comprising scandium, iron, and manganese comprising the following steps:

Step 1 adding acid and a reducing agent to an aqueous solution comprising scandium, iron, and manganese to convert any tetravalent manganese to divalent manganese forming an acid solution comprising said scandium, iron, and divalent manganese;
Step 2 converting any trivalent iron present in said acid solution comprising said scandium, iron, and divalent manganese from step 1 to divalent iron by adding an iron reducing agent forming a trivalent iron free acid solution comprising said scandium, divalent iron, and divalent manganese;
Step 3 adjusting said trivalent iron free solution comprising said scandium, divalent iron, and divalent manganese from step 2 to a pH from about 1.9 to about 2.1 to form a pH adjusted solution comprising said scandium, divalent iron, and divalent manganese;
Step 4 removing said scandium contained in said pH adjusted solution comprising said scandium, divalent iron, and divalent manganese from step 3 by contacting said pH adjusted solution comprising said scandium, divalent iron, and divalent manganese with an ion exchange resin being in a hydrogen form and having an iminodiacetic acid functionality forming an ion exchange resin having said scandium absorbed thereon;
Step 5 rinsing said ion exchange resin having said scandium absorbed thereon from step 4 with a dilute acid having a pH from about 1.9 to about 2.1 to remove any base metals and rare earth metals absorbed on said ion exchange resin without removing said scandium absorbed thereon;
Step 6 eluting said scandium absorbed on said ion exchange resin with a solution comprising a chelating agent to form an elution solution comprising said scandium and said chelating agent;
Step 7 precipitating said scandium from said elution solution comprising said scandium by adding a precipitating agent to said elution solution comprising said scandium to form a scandium precipitate in said elution solution;
and
Step 8 separating said scandium precipitate from said elution solution.

6 more elements

A method of recovering scandium from an aqueous solution comprising scandium, iron, and manganese comprising the following steps:

Step 1 adding acid and a reducing agent to said aqueous solution comprising scandium, iron, and manganese to convert any tetravalent manganese to divalent manganese forming an acid solution comprising said scandium, iron, and divalent manganese;
Step 2 converting any trivalent iron present in said acid solution comprising said scandium, iron, and divalent manganese from step 1 to divalent iron by adding an iron reducing agent forming a trivalent iron free acid solution comprising said scandium, divalent iron, and divalent manganese;
Step 3 adjusting said trivalent iron free solution comprising said scandium, divalent iron, and divalent manganese from step 2 to a pH from about 1.9 to about 2.1 to form a pH adjusted solution comprising said scandium, divalent iron, and divalent manganese;
Step 4 removing said scandium contained in said pH adjusted solution comprising said scandium, divalent iron, and divalent manganese from step 3 by contacting said pH adjusted solution comprising said scandium, divalent iron, and divalent manganese with an ion exchange resin being in a hydrogen form and having an iminodiacetic acid functionality forming an ion exchange resin having said scandium absorbed thereon;
Step 5 rinsing said ion exchange resin having said scandium absorbed thereon from step 4 with a dilute acid having a pH from about 1.9 to about 2.1 to remove any base metals and rare earth metals absorbed on said ion exchange resin without removing said scandium absorbed thereon;
Step 6 eluting said scandium absorbed on said ion exchange resin with a solution comprising a chelating agent to form an elution solution comprising said scandium and said chelating agent;
Step 7 removing said scandium from said elution solution comprising said scandium and said chelating agent by contacting said elution solution comprising said scandium and said chelating agent with a strong cation ion exchange resin being in a hydrogen form to form a strong cation ion exchange resin having said scandium absorbed thereon;
Step 8 eluting said scandium absorbed on said strong cation exchange resin from step 7 with a strong acid to form a second acid solution comprising said scandium;
Step 9 precipitating said scandium from said second acid solution comprising said scandium by adding a precipitating agent to said second acid solution comprising said scandium to form a scandium precipitate in a second acid solution;
and
Step 10 separating said scandium precipitate from said strong acid solution.

8 more elements

Dependencies are inferred from the claim text.