Method for making mat-molded rim parts
AssigneeThe Dow Chemical Company
InventorsLouis M. Alberino, Peter S. Carleton, Douglas P. Waszeciak
Life of this patent
Estimating the term…
Abstract
A process for the preparation of molded high strength composites comprising fibrous reinforcing material impregnated with a reaction injection molded polyisocyanurate resin. The process comprises first evacuating a mold containing the fibrous reinforcing material said mold equipped with means for accepting an overflow volume of the resin. The mold system is pressurized prior to gelation causing the overflow volume to be forced into a final volume. The molded composites have a high flexural moduli, good physical properties, low void content and smooth surface.
Claims17
A process for the preparation of a high strength composite comprising fibrous reinforcing material impregnated with a reaction injection molded polyisocyanurate resin said process comprising:
- a. providing a mold containing said fibrous reinforcing material and said mold equipped with means for decreasing an overflow volume of polyisocyanurate resin forming ingredients received to a final volume of said ingredients wherein the increment between said final volume and said overflow volume is from about 2 percent to about 15 percent of said final volume;
- b. evacuating said mold;
- c. injecting into said evacuated mold said resin forming ingredients in an amount in excess of that required to fill said final volume thereby causing said overflow volume;
- d. pressurizing said mold to a pressure of from about 50 to about 300 psi prior to gelation of said resin forming ingredients thereby causing a decrease in at least a portion of said overflow volume;
- and
- e. maintaining said pressure at least until said gelation has occurred.
A process for the preparation of a high strength composite comprising at least one fiber glass mat impregnated with a reaction injection molded polyisocyanurate resin said process comprising the steps of:
- a. providing a mold containing said at least one fiber glass mat and said mold equipped with a reservoir for receiving an overflow volume of polyisocyanurate resin forming ingredients and having an inlet for applying a positive gas pressure to said mold via said reservoir to decrease said overflow volume to a final volume of said ingredients wherein the increment between said final volume and said overflow volume is from about 2 percent to about 15 percent of said final volume;
- b. evacuating said mold and reservoir to a pressure of from about 0.01 to about 50 mm. of mercury;
- c. injecting into said evacuated mold polyisocyanurate resin forming ingredients comprising an aromatic polyisocyanate, less than a stoichiometric amount of at least one polyol and an isocyanate trimerization catalyst in an amount in excess of that required to fill said final volume thereby causing said overflow volume in said reservoir;
- d. pressurizing said mold prior to gelation of said resin forming ingredients by applying a pressure of from about 50 to about 300 psi of nitrogen to said reservoir thereby causing a decrease in at least a portion of said overflow volume to said final volume;
- and
- e. maintaining said pressure at least until said gelation has occurred.
Dependencies are inferred from the claim text.