Synthetic elastomer with improved chemical, aging and oil resistance
AssigneeHughes Tool Company
InventorRaymond L. Guzy
Life of this patent
Estimating the term…
Abstract
Ethylene propylene copolymer elastomers and ethylene propylene diene terpolymer elastomers are shown which, when cured, exhibit improved oil resistance and chemical aging properties at elevated temperatures and pressures. A previously polymerized liquid 1,2-polybutadiene is incorporated into the elastomer by chemical blending during the polymerization process. Such compositions are useful as electrical insulating materials for use under extreme environmental conditions, particularly in wire and cable constructions.
Claims6
A method of manufacturing a peroxide curable synthetic elastomer with improved chemical aging and oil resistance properties, comprising the steps of:
- reacting ethylene, propylene and a diene monomer in a solvent solution in the presence of a suitable catalyst;
- forming a water slurry product of the resulting ethylene-propylene-nonconjugated diene monomer terpolymer;
- and
- solution blending a liquid, high vinyl 1,2-polybutadiene resin with the terpolymer product by adding the 1,2-polybutadiene to the slurry prior to separating and drying the terpolymer elastomer, the 1,2-polybutadiene having at least about 80 mole % 1,2 vinyl structure with a pendant vinyl group for every other chain carbon.
A method of manufacturing a peroxide curable synthetic elastomer with improved chemical aging and oil resistance properties, comprising the steps of:
- reacting ethylene, propylene and a diene monomer in a solvent solution in the presence of a suitable catalyst to form an ethylene-propylene-nonconjugated diene monomer terpolymer;
- stopping the reaction by deactivating the catalyst and forming water slurry product;
- adding a liquid, high vinyl 1,2-polybutadiene resin to the slurry product to provide additional cure sites on the resulting elastomer, the 1,2-polybutadiene having at least about 80 mole % 1,2 vinyl structure with a pendant vinyl group for every other chain carbon;
- and
- separating and drying the elastomer.
A method of manufacturing a peroxide curable synthetic elastomer with improved chemical aging and oil resistance properties, comprising the steps of:
- reacting ethylene, propylene and a diene monomer in a solvent solution in the presence of a suitable catalyst to form an ethylene-propylene-nonconjugated diene monomer terpolymer;
- stopping the reaction by deactivating the catalyst;
- adding water to the solvent solution containing the terpolymer to form a water slurry of the elastomer;
- adding a liquid, high vinyl 1,2-polybutadiene resin to the slurry product to provide additional cure sites on the resulting elastomer, the 1,2-polybutadiene having at least about 80 mole % 1,2 vinyl structure with a pendant vinyl group for every other chain carbon;
- and
- separating and drying the resulting elastomer;
- and
- curing the elastomer with a peroxide curing agent.
A method of manufacturing a peroxide curable synthetic elastomer with improved chemical aging and oil resistance properties, comprising the steps of:
- reacting ethylene, propylene and a diene monomer in a solvent solution in the presence of a vanadium catalyst to form an ethylenepropylene-nonconjugated diene monomer terpolymer, the terpolymer having an ethylene/propylene ratio in the range of 20/80 to 80/20 and from about 2 to 20 weight percent of the terpolymer of the nonconjugated diene monomer;
- stopping the reaction by deactivating the catalyst;
- adding water to the solvent solution containing the terpolymer to form a water slurry of the terpolymer;
- adding a liquid, high vinyl 1,2-polybutadiene resin to the slurry product to provide additional cure sites on the resulting elastomer, the 1,2-polybutadiene having at least about 90 mole % 1,2 vinyl structure with a pendant vinyl group for every other chain carbon;
- and
- adding an extender oil to the slurry containing the terpolymer product;
- separating and drying the resulting elastomer;
- and
- curing the elastomer with a peroxide curing agent.
Dependencies are inferred from the claim text.