Treatment of electroless nickel plating baths
AssigneeOccidental Chemical Corporation
InventorsWei-chi Ying, Robert R. Bonk
Life of this patent
Estimating the term…
Abstract
A process for removing nickel and phosphorus species from a spent electroless nickel plating solution is described. This process involves an initial precipitation of phosphite values from the plating solution, followed by oxidation of hypophosphite and remaining phosphite to phosphate values, and the final removal of phosphate and nickel by lime precipitation. The treated plating solution is then separated from the precipitants, such as by filtration, and preferbly contain less than 1 milligrams/liter of nickel and/or total phosphorus species. This process is a cost effective method for treating spent electroless nickel plating solutions which is readily adaptable for on-site use.
Claims7
A process for removing nickel and phosphorus values including hypophosphite and phosphite species from spent electroless nickel plating solutions comprises the steps of:
- (a) contacting the spent plating solution with an effective amount of lime or calcium hydroxide to precipitate said phosphit species,
- (b) removing the precipitated phosphite species from the plating solution, wherein a major position of the total phosphite species present in the spent plating solution are removed,
- (c) contacting the treated plating solution of step (b) with an effective amount of potassium permanganate to convert said hypophosphite and phosphite species to phosphate species,
- (d) contacting the oxidized plating solution with an effective amount of lime or calcium hydroxide to precipitate said phosphate species and said nickel values, and
- (e) separating the precipitated phosphate species and nickel values from the treated solution of step (d) to produce an environmentally acceptable spent plating solution which is suitable for disposal.