US 4,788,236 AGranted
Process for producing particulate novolac resins and aqueous dispersions
AssigneeUnion Carbide Corporation
InventorPeter W. Kopf
Life of this patent
Estimating the term…
Abstract
Particulate novolac resins and aqueous dispersions are produced by condensing phenol with aldehyde using acid catalysis. Following neutralization, particulate novolac resin is formed by adding protective colloid to the aqueous mixture. Resin particle isolation can be aided by dephenolation.
Claims4
A process for producing particulate novolac resin comprising steps of:
- (a) condensing phenol with an aldehyde in the presence of a catalyst under acidic conditions to produce a novolac resin;
- (b) adding water before, during or after the condensation reaction step (a) to provide a novolac resin/water mixture;
- (c) neutralizing the acid catalyzed novolac resin using a base;
- (d) forming a particulate novolac resin dispersion by adding an effective amount of protective colloid to the aqueous mixture wherein the protective colloid is a polysaccharide selected from the group consisting of gum arabic, gum ghatti, gum tragacanth, and guar gum or it hydroxypropylate derivative;
- and (e) isolating the particulate novolac resin from the aqueous dispersion;
- said process including dephenolating the particulate novolac resin by separating out a sufficient amount of unreacted phenol prior to isolation of the resin so that less than about 6 percent of unreacted phenol remains in the dispersion.
3 more elements
A process for producing particulate novolac resin comprising the steps of:
- (a) condensing phenol with an aldehyde in the presence of an alkylated diphenyl oxide sulfonic acid or its corresponding salt as the catalyst under acidic conditions to produce a novolac resin;
- (b) adding water before, during or after the condensation reaction step (a) to provide a novolac resin/water mixture;
- (c) neutralizing the acid catalyzed novolac resin using a base;
- (d) forming a particulate novolac resin dispersion by adding an effective amount of protective colloid to the aqueous mixture wherein the protective colloid is a polysaccharide selected from the group consisting of gum arabic, gum ghatti, gum tragacanth, and guar gum or its hydroxypropylate derivative;
- and (e) isolating the particulate novolac resin from the aqueous dispersion.
2 more elements
A particulate novolac resin aqueous dispersion comprising:
- (1) the acid catalyzed condensation product of phenol and an aldehyde;
- (2) a neutralizing agent;
- (3) a protective colloid which is a polysaccharide selected from the group consisting of gum arabic, gum ghatti, gum tragacanth, and guar gum or its hydroxypropylate derivartive;
- (4) a catalyst comprising an alkylated diphenyl oxide sulfonic acid or its corresponding salt;
- and (5) a sufficient amount of water to produce a resin-in-water dispersion.
2 more elements