Composite by compression

A process for producing a composite having a composition consisting essentially of from about 40% by volume to about 60% by volume of polycrystalline inorganic filler phase consisting essentially of particles and/or filaments and from about 40% by volume to about 60% by volume of continuous interconnecting polycrystalline alkaline earth silicate matrix phase, said composite containing amorphous glassy phase in an amount of less than about 5% by volume of said composite, said matrix phase enveloping more than 50% by volume of the individual filler particles and//or filaments, said composite having a porosity of less than about 10% by volume, which consists essentially of forming a mixture of a polycrystalline inorganic filler in the form of particles and/or filaments and an alkaline earth silicate in amounts required to produce said composite, said filler being selected from the group consisting of boron carbide, chromium carbide, hafnium carbide, niobium carbide, silicon carbide, tantalum carbide, titanim carbide, vanadium carbide, zirconium carbide, hafnium nitride, niobium nitride, silicon nitride, tantalum nitride, titanium nitride, vanadium nitride, zirconium nitride, hafnium boride, niobium boride, tantalum boride, titanium boride, vanadium boride, zirconium boride, TaSi.sub.2, MoSi.sub.2, WSi.sub.2 and a mixture thereof, said alkaline earth silicate being represented by the stoichiometric formula xMO.zSiO.sub.2 where M=Ba, Ca, Mg, Sr and a mixture thereof, where x is 1, 2 or 3 and z is 1, 2 or 3, and wherein said MO and SiO.sub.2 constituent of said stoichiometric formula ranges to less than .+-.10% from said stoichiometric formula, said alkaline earth silicate having a melting point ranging from about 1250.degree. C. to about 1850.degree. C., said filler being a solid in said process and not significantly affected by said process, and injection molding said mixture at a temperature at which said alkaline earth silicate is molten ranging from about 1300.degree. C. to about 1900.degree. C. under a pressure sufficient to produce a product having the composition of said composite, said injection molding being carried out in a protective atmosphere or vacuum in which said filler and alkaline earth silicate are substantially inert thereby producing said composite free of reaction product detectable by scanning electron microscopy of said filler and alkaline earth silicate, and cooling said product to produce said composite.

A composite having a porosity of less than about 5% by volume consisting essentially of polycrystalline inorganic filler in the form of particles and/or filaments ranging in amount from greater than about 70% by volume to about 90% by volume of said composite, and a continuous interconnecting polycrystalline alkaline earth silicate matrix phase ranging in amount from about 10% by volume to less than about 30% by volume of said composite, said filler being selected from the group consisting of boron carbide, chromium carbide, hafnium, carbide, niobium, carbide, silicon carbide, tantalum carbide, titanium carbide, vanadium carbide, zirconium carbide, hafnium nitride, niobium nitride, silicon nitride, tantalum nitride, titanium nitride, vanadium nitride, zirconium nitride, hafnium boride, niobium boride, tantalum boride, titanium boride, vanadium boride, zirconium boride, TaSi.sub.2, MoSi.sub.2, WSi.sub.2 and a mixture thereof, said alkaline earth silicate phase being represented by the stoichiometric formula xMO.zSiO.sub.2 where M=Ba, Ca, Mg, Sr and a mixture and/or solution thereof, where x is 1, 2 or 3 and z is 1, 2 or 3, and wherein said MO and SiO.sub.2 constitutent of said stoichiometric formula ranges less than .+-.10% from said stoichiometirc formula, said alkaline earth silicate phase enveloping more than 50% by volume of the individual filler particles and/or filaments, said alkaline earth silicate phase having a melting point ranging from about 1250.degree. C. to about 1850.degree. C., said composite containing an amorphous glassy phase in an amount of less than aobut 5% by volume of said composite, said composite being free of reaction product detectable by scanning electron microscopy of said filler and matrix phase.