Process for producing dentures of denture parts and storable dental materials suitable for this
AssigneeUexkull & Stolberg
InventorsRudolf J. Michl, Peter Wollwage, Gerhard Zanghellini
Life of this patent
Estimating the term…
Abstract
A process for producing artificial teeth or parts thereof is given, in which a mass of at least one polyfunctional isocyanate, at least one polyol and at least one methacrylate monomer, as well as in each case one catalyst for the polymerization of the methacrylate monomer and for the acceleration of the formation of a urethane is hardened in a first stage to an elastic blank, which can then be cured in a second stage to artificial teeth or parts thereof. A storage-stable dental material for performing the process comprises two components, namely at least one polyfunctional isocyanate as the first component and the remaining constituents as the second component.
Claims11
A two stage process for producing artificial teeth or crowns, inlays or other tooth parts using a curable dental material, in which process the first stage comprises producing a rubbery elastic blank by hardening at ambient temperature a composition comprising
- (a) at least one polyfunctional isocyanate,
- (b) at least one polyol,
- (c) at least one methacrylate monomer having at least two hydroxyl groups,
- (d) a catalyst for the heat or light initiated polymerization of the methacrylate monomer, and
- (e) a catalyst for accelerating the formation of a polyurethane from (a), (b) and (c) which does not catalyze the radical polymerization of (c), shaping and mechanically finishing the blank, and the second stage comprises curing the shaped rubbery composition to provide said hard artificial teeth or parts thereof.
A storable dental fabrication material for producing artificial teeth or crowns, inlays or other tooth parts comprising a first separate component comprising
- (a) at least one polyfunctional isocyanate, and a second separate component comprising
- (b) at least one polyol,
- (c) at least one methacrylate monomer having at least two hydroxyl groups,
- (d) a catalyst for the heat or light initiated polymerization of the methacrylate monomer, and
- (e) a catalyst for acceleration of the formation of a polyurethane from constituents (a), (b) and (c) which does not catalyze the polymerization of the methacrylate monomer (c).
Dependencies are inferred from the claim text.