Casting powder for use in bottom pour ingot steel production and method for employing same
AssigneeAtlantic Metals Corporation
InventorsMaharaj K. Koul, Richard Paul
Life of this patent
Estimating the term…
Abstract
A casting powder for use in ingot steel production through bottom pour process is provided. The powder combines the crucial properties of existing bottom pour fluxes and hot topping compounds into a single, easily dispensed mixture. The present invention provides a significant simplifying and savings over present methods while producing steel with fewer impurities.
Claims7
A method for increased efficiency of protecting a steelmaker's mold and a steel ingot as bottom poured into the mold, including protecting against excessive piping of the steel which tends to occur when the molten steel cools too rapidly in the mold, comprising
- introducing into the mold a predetermined quantity of a casting powder, comprising chemical components combined to produce a bottom pour flux, and including an expandable graphite as at least 4.0% by weight of the composition of said casting powder,
- pouring molten steel into said mold and covered with said casting powder to cause a substantial portion of said casting powder to rise to the vicinity of the top of said mold, thinly coating the side walls of said mold as it rises, and expanding into a thick insulative blanket on top of the molten steel of a sufficient insulative quality of avoid a need for a hot topping compound, limiting the steel's rate of cooling and thereby minimizing the piping of the ingot;
- wherein said insulative quality is achieved through use of an expandable graphite that expands to 100-300 times its volume and comprises 4.0 to 12.0% by weight of the composition of said casting powder.
A casting powder employed in a mold for bottom pour steel ingot production, comprising
- a flux mixture of chemical components to produce a bottom pour flux which coats and protects the top and sides of molten steel as it is introduced into the mold, including an expandable graphite component as at least 4.0% by weight of the composition of said mixture, and
- which flux expands to form a thick insulative blanket on top of the molten steel of sufficient insulative quality to avoid need for a hot topping compound, limiting the steel's rate of cooling and thereby minimizing piping of the ingot;
- wherein said insulative quality is achieved through use of an expandable graphite that expands to 100-300 times its volume and comprises 4.0 to 12.0% by weight of the composition of said mixture.
Dependencies are inferred from the claim text.