Aluminum alloy automotive material
AssigneeAluminum Company of America
InventorsM. E. Hyland, Warren H. Hunt, Jr.
Life of this patent
Estimating the term…
Abstract
Aluminum alloy products particularly for automotive applications, e.g. panel members, may be produced from a body of aluminum base alloy consisting essentially of, by weight, 0.5 to 0.85% Si, 0.25 to 0.48% Mg, 0.05 to 0.4% Fe, 0.75 to 1.1% Cu, 0.1 to 0.5 wt. % Mn, the balance essentially aluminum and incidental elements and impurities. The alloy body may be homogenized at a temperature in the range 900.degree. to 1100.degree. F. and thereafter worked into a wrought product such as sheet which may be continuously solution heat treated and quenched and aged to a T4 condition prior to forming into vehicular panel members, for example.
Claims40
A method of producing a vehicular structural member, comprising the steps of:
- (a) providing a body of aluminum base alloy consisting essentially of 0.5 to 0.85% Si, 0.25 to 0.48% Mg, 0.05 to 0.40% Fe, 0.7 to 1.1% Cu, 0.1 to 0.5 wt. % Mn, the balance essentially aluminum and incidental elements and impurities;
- (b) working said body to produce a wrought aluminum sheet product;
- (c) solution heat treating said wrought sheet aluminum product on a continuous basis at a temperature within the range of 900.degree. to 1100.degree. F. in order to produce a structure having a fine grain size;
- (d) quenching said sheet product;
- (e) aging said sheet product to a condition having a substantially stable level of mechanical properties to provide a solution heat treated, quenched and aged product having a 26 to 31% elongation, a yield strength in the range of 12 to 30 ksi, and capable of being formed in mild steel forming dies to produce a deep drawn product having a shape substantially identical to mild steel formed in said dies;
- and
- (f) forming said aged product in said condition into said structural member.
A method of producing a vehicular structural member, comprising the steps of:
- (a) providing a body of aluminum base alloy consisting essentially of 0.55 to 0.75% Si, 0.3 to 0.45% Mg, 0.05 to 0.40% Fe, 0.85 to 1.0% Cu, 0.1 to 0.5 wt. % Mn, the balance essentially aluminum and incidental elements and impurities;
- (b) working said body to produce a wrought aluminum sheet product;
- (c) solution heat treating said wrought sheet aluminum product on a continuous basis for a period of less than two minutes at a temperature within the range of 900.degree. to 1100.degree. F. in order to produce a structure having a fine grain size;
- (d) quenching said sheet product;
- (e) naturally aging said sheet product to a T4 condition to provide a solution heat treated, quenched and aged product having a 26 to 31% elongation, a yield strength in the range of 12 to 35 ksi, and capable of being formed in mild steel forming dies to produce a deep drawn product having a shape substantially identical to mild steel formed in said dies;
- and
- (f) forming said aged product in said T4 condition into said structural member and artificially aging said product at a temperature of 225.degree. to 500.degree. F., thereby increasing its strength.
A method of producing a plural panel vehicular structural member having spaced generally parallel inner and outer panels connected along peripheral portions thereof comprising the steps of:
- (a) providing a body of aluminum base alloy consisting essentially of 0.5 to 0.85% Si, 0.25 to 0.55% Mg, 0.05 to 0.40% Fe, 0.75 to 1.0% Cu, 0.1 to 0.4 wt. % Mn, the balance essentially aluminum and incidental elements and impurities;
- (b) homogenizing said body at a temperature in the range of 900.degree. to 1100.degree. F.;
- (c) hot rolling said body to produce a hot rolled sheet;
- (d) cold rolling said hot rolled sheet to provide a cold rolled sheet ranging in thickness between 0.019 and 0.077 inch;
- (e) solution heat treating said cold rolled sheet at a temperature within the range of 900.degree. to 1100.degree. F.;
- (f) quenching said sheet;
- (g) aging said sheet product to a condition having a substantially stable level of mechanical properties to provide a solution heat treated, quenched and aged product having a 26 to 31% elongation, a yield strength in the range of 12 to 35 ksi, and capable of being formed in mild steel forming dies to produce a deep drawn product having a shape substantially identical to mild steel formed in said dies;
- (h) forming a portion of such aged sheet product substantially at room temperature into an outer panel member by operations including stamping;
- (i) forming a further portion of such aged sheet product substantially at room temperature into an inner panel by operations including deep drawing in mild steel forming dies to produce a panel having raised and recessed portions imparting flexural stiffness thereto;
- (j) connecting said inner and outer panels together at peripheral portions thereof to provide a plural panel vehicular structural member;
- (k) applying a heat curable coating to at least one surface portion of said automotive structure;
- and
- (l) heating said vehicular structure to a temperature of 225.degree. to 500.degree. F. to cure said coating and to increase the strength of said plural panel vehicular structure.
In a method of producing a sheet product for forming into vehicular structural members wherein an aluminum alloy product is formed to produce said sheet, the improvement wherein said sheet is provided as an alloy consisting essentially of 0.5 to 0.85% Si, 0.25 to 0.48% Mg, 0.05 to 0.40% Fe, 0.75 to 1.0% Cu, 0.1 to 0.5 wt. % Mn, the balance essentially aluminum and incidental elements and impurities, said sheet further being provided in the condition resulting from:
- (a) working said body to produce a wrought aluminum sheet product;
- (b) solution heat treating said wrought sheet aluminum product on a continuous basis at a temperature within the range of 900.degree. to 1100.degree. F. in order to produce a structure having a fine grain size;
- (c) quenching said sheet product;
- and
- (d) aging said sheet product to a condition having a substantially stable level of mechanical properties to provide a solution heat treated, quenched and aged product having a 26 to 31% elongation, a yield strength in the range of 12 to 35 ksi, and capable of being formed in mild steel forming dies to produce a deep drawn product having a shape substantially identical to mild steel formed in said dies.
In the method of producing a vehicular panel wherein an aluminum alloy product is formed to produce said panel, the improvement wherein said product is provided as an alloy consisting essentially of 0.5 to 0.85 wt. % Si, 0.25 to 0.48 wt. % Mg, 0.05 to 0.40 wt. % Fe, 0.75 to 1.0 wt. % Cu, 0.1 to 0.4 wt. % Mn, the balance essentially aluminum and incidental elements and impurities, said product further being provided in the condition resulting from:
- (a) homogenizing a body of said alloy at a temperature in the range of 900.degree. to 1100.degree. F.;
- (b) hot rolling said body to produce a hot rolled sheet having a thickness in the range of 0.10 to 0.25 inch;
- (c) cold rolling said hot rolled sheet to provide a cold rolled sheet having a thickness in the range of 0.019 to 0.077 inch;
- (d) continuously heat treating said cold rolled sheet at a temperature in the range of 900.degree. to 1100.degree. F.;
- (e) quenching said sheet at a rate of at least 10.degree. F./sec. to a temperature of 350.degree. F. or less;
- and
- (f) aging said sheet product to a condition having a substantially stable level of mechanical properties to provide a solution heat treated, quenched and aged product having a 26 to 31% elongation, a yield strength in the range of 12 to 35 ksi, and capable of being formed in mild steel forming dies to produce a deep drawn product having a shape substantially identical to mild steel formed in said dies.
An alloy for vehicular structural members consisting essentially of 0.5 to 0.85% Si, 0.25 to 0.48% Mg, 0.05 to 0.40% Fe, 0.7 to 1.1% Cu, 0.1 to 0.4 wt. % Mn, the balance essentially aluminum and incidental elements and impurities.
A vehicular member comprised of aluminum base alloys consisting essentially of 0.5 to 0.85% Si, 0.25 to 0.55% Mg, 0.05 to 0.40% Fe, 0.7 to 1.1% Cu, 0.1 to 0.5 wt. % Mn, the balance essentially aluminum and incidental elements and impurities.
A sheet product suitable for fabricating into vehicular panel members, the sheet product comprised of an aluminum base alloy consisting essentially of 0.5 to 0.85% Si, 0.25 to 0.48% Mg, 0.05 to 0.40% Fe, 0.7 to 1.1% Cu, 0.1 to 0.5 wt. % Mn, the balance essentially aluminum and incidental elements and impurities.
Vehicular panel members fabricated from a sheet product consisting essentially of 0.5 to 0.85% Si, 0.25 to 0.48% Mg, 0.05 to 0.40% Fe, 0.7 to 1.1% Cu, 0.1 to 0.5 wt. % Mn, the balance essentially aluminum and incidental elements and impurities.
A plural panel vehicular structural member having spaced generally parallel inner and outer panels connected along peripheral portions thereof, said panels comprised of an alloy consisting essentially of 0.5 to 0.85% Si, 0.25 to 0.48% Mg, 0.05 to 0.40% Fe, 0.7 to 1.1% Cu, 0.1 to 0.5 wt. % Mn, the balance essentially aluminum and incidental elements and impurities and said inner panel being deep drawn product and formed in mild steel forming dies to produce said deep drawn product having a shape substantially identical to mild steel formed in said dies.
In the method of producing shaped vehicular members wherein a sheet product is shaped to produce a panel vehicular structural member, the improvement wherein said sheet product is provided in solution heat treated condition as an alloy consisting essentially of 0.5 to 0.85% Si, 0.25 to 0.48% Mg, 0.05 to 0.40% Fe, 0.7 to 1.1% Cu, 0.1 to 0.5 wt. % Mn, the balance essentially aluminum and incidental elements and impurities.