Process for laser hardfacing drill bit cones having hard cutter inserts
AssigneeSmith International, Inc.
InventorNaresh J. Kar
Life of this patent
Estimating the term…
Abstract
A cone blank for a rotary cone rock bit is forged, rough machined, carburized and heat-treated, followed by the formation of insert holes therein. Inserts are then pressed into the insert holes. The finished cone is subsequently sprayed with hardfacing cladding material in powdered form. The powder is thereafter densified and fused with a laser source to give a hard, erosion-resistant clad layer on the outer surface, including in the immediate vicinity of the inserts.
Claims14
A process for hardfacing a hard cutter insert bearing cone for a rock bit comprising the steps of:
- machining a cone blank surface;
- carburizing the bearing surfaces formed within the cone blank;
- heat-treating the cone blank to temper the cone blank to an exterior cone blank hardness of about 40 Rockwell C hardness units;
- forming holes in said cone blank surface for one or more insert cutters;
- pressing the inserts in the insert holes formed in the cone blank;
- finish machining the inner bore of the cone;
- applying a cladding material to the exterior surface of the finished cone blank;
- bombarding the cladding material to the exterior surface of the cone with a laser beam of sufficient intensity and for a sufficient time so as to melt the cladding material into the surface of the cone blank, light reflective means adjacent an exposed surface of said inserts, the exposed light reflective means ajacent the cutter inserts not being heated substantially in the step of subjecting the cladding material to the laser beam on to the exterior surface of the cone, the cladding material being immediately adjacent to said light reflective means adjacent said inserts;
- and
- cooling the cladding material sufficiently rapidly to form a hard external layer on said cone blank.
The process as set forth in claim 10 wherein the laser beam used in the step of bombarding has a beam diameter of approximately 0.4 inch.
A process for hardfacing a downhole cutter tool having one or more hard cutter inserts extending from a surface of the tool comprising the steps of:
- Machining the outer surface of a downhole tool blank;
- heat-treating the tool blank to temper the blank to an exterior tool blank hardness of about 40 Rockwell C hardness units;
- forming insert holes in the surface of said downhole tool for said one or more inserts;
- inserting said inserts into said insert holes formed by said downhole tool;
- applying a cladding material to the exterior surface of said downhole tool;
- bombarding the cladding material to the exterior surface of said downhole tool with a laser beam of sufficient intensity and for a sufficient time so as to melt the cladding material into the surface of the downhole tool, light reflective means adjacent an exposed surface of said one or more inserts, the exposed light reflective means adjacent the cutter inserts not being heated substantially in the step of subjecting the cladding material to the laser beam on the exterior surface of the downhole tool, the cladding material being immediately adjacent to said light reflective inserts;
- and
- cooling the cladding material sufficiently rapidly to form a hard external layer on said downhole tool.
Dependencies are inferred from the claim text.