Polymer article having an antibacterial property containing zeolite particles therein and the processes for producing same
AssigneeKanebo Ltd./Kanto Chemical Co.
InventorsZenji Hagiwara, Shigetaka Hoshino, Hiroo Ishino, Saburo Nohara, Kenichi Tagawa, Keio Yamanaka
Life of this patent
Estimating the term…
Abstract
A polymer article containing zeolite particles on which metal ion having a bactericidal property, e.g. Ag, Cu or Zn, is provided by an ion exchange reaction shows an excellent bactericidal effect and durability of the effect, but no deterioration of physical properties of the polymer. The polymer article is produced by admixing zeolite particles previously provided with the metal ion with a polymer or by moulding a zeolite-containing polymer into an article and then treating the article with a metal ion solution.
Claims15
A polymer article having antibacterial properties in which the polymer article comprise at least one polymer and 0.01 to 10% by weight, based on the total weight of the polymer article, of zeolite particles having a specific surface area of at least 150 m.sup.2 /g, based upon anhydrous zeolite as the standard, and an SiO.sub.2 /Al.sub.2 O.sub.3 mol ratio of at most 14, provided that the zeolite particles retain at least one metal ion having bacteriocidal properties at ion-exchangeable sites of the zeolite in an amount less than 92 percent of the ion exchange capacity of the zeolite.
A shaped article in the form of a fiber, a film or a granule having antibacterial properties consisting essentially, in percent by weight of the entire shaped article, of:
- 90 to 99.9% of a polymeric substrate having dispersed therein;
- from 0.1 to 10% of zeolite particles having a specific surface are of at least 150 m.sup.2 /g, based upon anhydrous zeolite as the standard, and an SiO.sub.2 /Al.sub.2 O.sub.3 mol ratio of at most 14, wherein the zeolite particles retain at least one metal ion having bacteriocidal properties at ion-exchangeable sites of the zeolite in an amount less than 92 percent of the ion exchange capacity of the zeolite.
A process for producing a polymer article having antibacterial properties in which the polymer article comprises at least one polymer and 0.1 to 10% by weight, based on the total weight of the polymer article, of zeolite particles having a specific surface area of at least 150 m.sup.2 /g, based upon anhydrous zeolite as the standard, and an SiO.sub.2 /Al.sub.2 O.sub.3 mol ratio of at most 14, wherein the zeolite particles retain at least one metal ion having bacteriocidal properties at ion-exchangeable sites of the zeolite in an amount less than 92 percent of the ion exchange capacity of the zeolite, said process comprising the steps of:
- (a) admixing the zeolite particles, which retain at least one metal ion having bacteriocidal properties at ion-exchangeable sites of the zeolite in an amount less than 92 percent of the ion exchange capacity of the zeolite, with the polymer or a mixture of such polymers, and thereafter
- (b) moulding the polymer/zeolite admixture to form a shaped article.
A process for producing a polymer article having antibacterial properties in which the polymer article comprises at least one polymer and 0.01 to 10% by weight, based on the total weight of the polymer article, of zeolite particles having a specific surface area of at least 150 m.sup.2 /g, based upon anhydrous zeolite as the standard, and an SiO.sub.2 /Al.sub.2 O.sub.3 mol ratio of at most 14, said process comprising the steps of:
- (a) molding a polymer or a mixture of polymers containing said zeolite particles dispersed therein, and then
- (b) treating the thus-molded article with an aqueous solution of at least one water-soluble salt of at least one metal ion having bacteriocidal properties to provide the zeolite particles with said metal ion at ion-exchangeable sites of the zeolite in an amount less than 92 percent of the ion exchange capacity of the zeolite.