Back to results
US 4,773,466 AGranted
Process for preparing polycarbonate copolymer foam suitable for lost foam casting
AssigneeArco Chemical Company
InventorsMichael J. Cannarsa, Haven S. Kesling, Jr., Hsiang-Ning Sun
Life of this patent
Estimating the term…
Abstract
The evaporative casting of molten metals has been shown to produce castings having smooth surfaces without any sign of carbon deposits thereon by using a copolymer polycarbonate prepared from cyclohexene oxide, cyclopentene oxide, cycloheptene oxide, or isobutylene oxide and carbon dioxide.
Claims7
A process for preparing a pattern for use in making metal castings which have no residual carbon on the surface comprising
- (a) selecting a copolymer polycarbonate of general formula which is selected from the group consists of ##STR3## and ##STR4## where n is 3, 4, or 5, x is in the range of 100 to 500, the number average molecular weight is in the range 15,000 to 100,000, said polymer has only a single glass transition temperature in the range 85-130.degree. C.,
- (b) forming said copolymer into particles having a bead size between 100 and 1000 microns in diameter,
- (c) suspending said particles in water using a suitable suspending agent system,
- (d) adding a suitable blowing agent to the suspension and heating to impregnate the particles,
- (e) separating the impregnated beads from the aqueous suspension, washing and drying the beads,
- (f) pre-expanding the beads by subjecting to atmospheric steam to obtain a density of about 1 to about 4 pounds per cubic foot,
- (g) aging the beads, and
- (h) molding the beads into the desired pattern having a density of about 3.0 pcf or less.
5 more elements
Dependencies are inferred from the claim text.