Process for producing luminous material based on manganese activated cadmium borate
AssigneeDegussa AG
InventorsAkos Kiss, Peter Kleinschmit, Werner Volker, Gunter Halbritter
Life of this patent
Estimating the term…
Abstract
There are prepared luminescent materials based on cadmium borate activated with manganese which is insensitive to impurities, temperature stable, not sensitive to grinding, and stable to ceramic glazes having the composition. In the preparation, the manganese activator is added in the form of a zeolite.
Claims8
A process for producing a luminescent material containing manganese activated cadmium borate comprising the steps of:
- (1) forming a mixture in comminuted form corresponding to the formulation of
- (a) 1 to 80 mole % cadmium oxide (CdO),
- (b) 1 to 50 mole % boron oxide (B.sub.2 O.sub.3),
- (c) 0.2 to 1.3 mole % manganese oxide (MnO),
- (d) 0 to 10 mole % of an oxide selected from the group potassium oxide, calcium oxide, magnesium oxide, barium oxide, strontium oxide, nickel oxide, cobalt oxide, chromium oxide, titanium oxide, and zirconium oxide,
- (e) 0.1 to 22.5 mole % sodium oxide (Na.sub.2 O),
- (f) 0.3 to 23.8 mole % aluminum oxide (Al.sub.2 O.sub.3),
- (g) 0.5 to 47.5 mole % silica (SiO.sub.2);
- wherein materials (a), (b) and (d) are oxides or compounds which are converted into oxides under the calcining conditions employed in step (3) and materials (c), (e), (f) and (g) are in the form of a manganese loaded zeolite-A;
- (2) lightly pressing the mixture of step (1);
- and
- (3) calcining in air the lightly pressed mixture of step (2) at 650.degree. C. to 900.degree. C. for 0.5 to 6 hours.
9 more elements
A process for producing a luminescent material containing manganese activated cadmium borate comprising the steps of:
- (1) forming a mixture is comminuted form corresponding to the formulation of
- (a) 1 to 80 mole % cadmium oxide (CdO),
- (b) 1 to 50 mole % boron oxide (B.sub.2 O.sub.3),
- (c) 0.2 to 1.3 mole % manganese oxide (MnO),
- (d) 0.1 to 22.5 mole % sodium oxide (Na.sub.2 O),
- (e) 0.3 to 23.8 mole % aluminum oxide (Al.sub.2 O.sub.3),
- (f) 0.5 to 47.5 mole % silica (SiO.sub.2), wherein materials (a), and (b) are compounds which are oxides or compounds which are converted into oxides under the calcining conditions employed in step (3) and materials (c), (d), (e) and (f) are in the form of a manganese loaded zeolite-A
- (2) lightly pressing the mixture of step (1);
- and
- (3) calcining in air the lightly pressed mixture of step (2), at 650.degree. C. to 900.degree. C. for 0.5 to 6 hours.
7 more elements