AssigneeThe United States of America as represented by the United States Department of Energy
InventorsAmbrose H. Ballard, Thomas G. Godfrey, Jr., Erb H. Mowery
Estimating the term…
The hot pressing of beryllium oxide powder into high density compacts with little or no density gradients is achieved by employing a homogeneous blend of beryllium oxide powder with a lithium oxide sintering agent. The lithium oxide sintering agent is uniformly dispersed throughout the beryllium oxide powder by mixing lithium hydroxide in an aqueous solution with beryllium oxide powder. The lithium hydroxide is converted in situ to lithium carbonate by contacting or flooding the beryllium oxide-lithium hydroxide blend with a stream of carbon dioxide. The lithium carbonate is converted to lithium oxide while remaining fixed to the beryllium oxide particles during the hot pressing step to assure uniform density throughout the compact.
A method for preparing an article of beryllium oxide by hot pressing comprising the steps of forming a homogeneous mixture of about 98.5 to 99.5 weight percent of beryllium oxide particulates and sufficient lithium hydroxide in an aqueous solution to provide about 0.25 to 1.5 weight percent equivalent of lithium oxide, contacting the mixture with carbon dioxide for a sufficient duration to convert in situ essentially all the lithium hydroxide to lithium carbonate, and thereafter hot pressing the mixture into an article of desired configuration of near theoretical density, said hot pressing step being characterized by the lithium carbonate being uniformly dispersed throughout the mixture and affixed to the beryllium oxide particulates and converting to lithium oxide during the hot pressing step to provide essentially uniform sintering of the beryllium oxide particulates for providing the article with essentially uniform density.
Dependencies are inferred from the claim text.