Loading patent…
AssigneeNippon Shokubai Kagaku Kogyo Co., Ltd.
InventorsKoichi Saito, Kenji Ueda, Yasuo Ikeda
Estimating the term…
An exhaust gas cleaning catalyst composed of a refractory three-dimensional structure and a catalytically active substance supported thereon. That surface or part of the catalyst which makes contact with an exhaust gas is formed of numerous irregularly arranged protrusions composed of a refractory inorganic powder having a particle diameter of 5 to 300 micrometers or a mixture of it with refractory inorganic fibers and the catalytically active substance supported on the protrusions. The catalyst can be produced, for example, by preparing an aqueous slurry from the refractory inorganic powder having a particle diameter of 5 to 300 micrometers or a mixture of it with the refractory inorganic fibers and a suitable dispersant, forming numerous irregularly arranged protrusions on that surface or part of a refractory three-dimensional structure which makes contact with an exhaust gas by using the resulting slurry, drying the structure optionally followed by calcination, depositing the catalytically active substance, and drying and calcining the resulting structure.
An exhaust gas cleaning catalyst composed of a refractory three-dimensional structure and a catalytically active substance supported thereon, wherein that surface or part of the catalyst which makes contact with an exhaust gas is formed of numerous irregularly arranged protrusions composed of a refractory inorganic powder having a particle diameter of 5 to 300 micrometers or a mixture of it with refractory inorganic fibers and the catalytically active substance supported on the protrusions.
A process for producing an exhaust gas cleaning catalyst comprising a refractory three-dimensional structure and a catalytically active substance supported thereon, which comprises depositing the catalytically active substance on a refractory inorganic powder having a particle diameter of 5 to 300 micrometers or a mixture of it with refractory inorganic fibers, preparing an aqueous slurry from the resulting mixture and at least one dispersant selected from the group consisting of alumina sol, titania sol, zirconia sol, silica sol, soluble boehmite and soluble organic polymer compounds, forming numerous irregularly arranged protrusions on that surface or part of the refractory three-dimensional structure which makes contact with an exhaust gas by using the resulting slurry, and drying and calcining the resulting structure.
A process for producing an exhaust gas cleaning catalyst comprising a refractory three-dimensional structure and a catalytically active substance supported thereon, which comprises preparing an aqueous slurry from a refractory inorganic powder having a particle diameter of 5 to 300 micrometers or a mixture of it with refractory inorganic fibers and at least one dispersant selected from the group consisting of alumina sol, titania sol, zirconia sol, silica sol, soluble boehmite and soluble organic polymer compounds, forming numerous irregularly arranged protrusions on that surface or part of the refractory three-dimensional structure which makes contact with an exhaust gas by using the resulting slurry, drying the structure, optionally calcining it, depositing the catalytically active substance on the structure, and drying and calcining the resulting structure.
Dependencies are inferred from the claim text.