Method of molding optical lenses
OwnerTetsuro Izumitani, Shinichiro Hirota +2inventors
InventorsTetsuro Izumitani, Shinichiro Hirota, Helmuth E. Meissner, Kishio Sugawara
Life of this patent
Estimating the term…
Abstract
Optical lenses high in configurational accuracy with smooth surfaces are press molded in a carefully finished, polished and properly dimensioned mold preferably in a non-oxidizing atmosphere. The molding operation includes placing a quantity of glass having an internal viscosity of at least about 10.sup.6 poises in such a mold while maintaining the mold at a temperature at least equal to the glass transition temperature and thereafter passing the glass into a lens of predetermined configuration at a pressure of at least 100 Kg/cm.sup.2. Performing procedures are also disclosed.
Claims1
A method of molding an optical lens comprising
- (a) heating a piece of glass until the heated glass has an inside viscosity within the range of 10.sup.6 to 10.sup.7.8 poises;
- (b) placing the glass into a mold having at least one optical quality surface while maintaining the mold at a temperature at least equal to the glass transition temperature;
- (c) preform forming the glass in the mold to give the glass an external form generally equal to the final form desired by pressing the glass while the inside viscosity of the glass is in the range of 10.sup.7.5 to 10.sup.9 poises;
- and
- (d) pressing and molding the glass into the predetermined lens configuration at a pressure of at least 100 kg/cm.sup.2 while maintaining the inside viscosity of the glass between 10.sup.7.5 and 10.sup.11 poises.
Dependencies are inferred from the claim text.