Immobilization of lead and cadmium in solid residues from the combustion of refuse using lime and phosphate
AssigneeWheelabrator Environmental Systems, Inc.
InventorsMark J. O'Hara, Marion R. Surgi
Life of this patent
Estimating the term…
Abstract
Solid residues arising from the burning of solid wastes have lead and cadmium sufficiently insolubilized to pass the EPA toxicity test only where the pH in the EPA test is between 7.5 and 12.0. Addition of water soluble phosphate, especially phosphoric acid, increases the immobilization of lead and cadmium so as to make such residues in compliance with the toxicity tests over a substantially broader pH range.
Claims17
A method of immobilizing lead and cadmium in a free flowing particulate dry solid residue which maintains its free flowing particulate nature after the immobilizing treatment, said dry solid residue comprising fly ash and mixtures of fly ash with bottom ash resulting from the incineration of municipal waste, comprising contacting the dry solid residue with at least one water soluble phosphate in an amount equivalent to about 1 to about 8% by weight of phosphoric acid based on the total residue in the presence of a free lime source selected from the group consisting of lime, hydrated lime, flue gas scrubber product, and combinations thereof, in an amount sufficient to furnish from about 1 to about 25 parts by weight calcium hydroxide per 5 parts by weight of fly ash whereby the leaching of cadmium and lead is reduced to a level no more than 1 ppm cadmium and 5 ppm lead as determined in an EPA test performed on the resulting dry treated residue.
A method of immobilizing lead and cadmium as a free flowing particulate mass in a free flowing dry particulate mass of a fly ash and bottom ash mixture where each said ash results from the incineration of municipal waste in a mass burning facility comprising contacting the dry ash mixture with at least one water soluble phosphate in an amount equivalent to about 1 to about 8 percent by weight of phosphoric acid based on the total ash mixture in the presence of a free lime source selected from the group consisting of lime, hydrated lime, flue gas scrubber products, and combinations thereof, in an amount sufficient to furnish from about 1 to about 25 parts by weight of calcium hydroxide per 5 parts by weight of fly ash whereby the leaching of cadmium and lead is reduced to a level no more than 1 ppm cadmium and 5 ppm lead as determined in an EPA test performed on the resulting treated ash mixture.