Copper-silver-titanium-tin filler metal for direct brazing of structural ceramics
AssigneeThe United States of America as represented by the United States Department of Energy
InventorArthur J. Moorhead
Life of this patent
Estimating the term…
Abstract
A method of joining ceramics and metals to themselves and to one another at about 800.degree. C. is described using a brazing filler metal consisting essentially of 35 to 50 at. % copper, 40 to 50 at. % silver, 1 to 15 at. % titanium, and 2 to 8 at. % tin. This method produces strong joints that can withstand high service temperatures and oxidizing environments.
Claims3
A brazing filler alloy having a low brazing temperature for directly joining ceramics to metals comprising 35 to 50 at. % copper, 40 to 50 at. % silver, 1 to 15 at. % titanium and 2 to 8 at. % tin.
A method of joining ceramic and metal components comprising assembling surfaces of components to be joined in an abutting relationship with a brazing filler metal disposed thereinbetween, said brazing filler metal consisting essentially of 35 to 50 at. % copper, 40 to 50 at. % silver, 1 to 15 at. % titanium, and 2 to 8 at. % tin heating the resulting assembly to a brazing temperature in the range of 800.degree. to 850.degree. C. under nonoxidizing conditions and cooling the resulting braze joint.
A composite body comprising at least two structural components of ceramics and metals joined with brazing filler metal disposed thereinbetween consisting essentially of 35 to 50 at. % copper, 40 to 50 at. % silver, 1 to 15 at. % titanium, and 2 to 8 at. % tin.
Dependencies are inferred from the claim text.