Permanent-magnetic material

A method for the production of a permanent-magnet material, characterized by combining pertinent metallic elements as component raw materials in proportions indicated by the following formula:

• R(Co.sub.1-X-Y-.alpha.-.beta. Fe.sub.X Cu.sub.y M.sub..alpha. M'.sub..beta.).sub.A
• (wherein X, Y, .alpha., .beta., and A respectively represent the following numbers:
• 0.01.ltoreq.X, 0.02.ltoreq.Y.ltoreq.0.25, 0.001.ltoreq..alpha..ltoreq.0.15,
• 0.0001.ltoreq..beta..ltoreq.0.001, and 6.0.ltoreq.A.ltoreq.8.3,
• providing that the amount of Fe to be added should be less than 15% by weight, based on the total amount of the composition, and R, M, and M' respectively represent the following constituents:
• R:
• At last one element selected from the group of rare earth elements,
• M:
• At least one element selected from the group consisting of Ti, Zr, Hf, Nb, V, and Ta, and
• M':
• B or B+Si),
• melting and casting the resultant mixture in an inert atmosphere thereby obtaining an ingot, coarsely crushing said ingot into coarse particles, finely comminuting said coarse particles into fine particles having particle diameters of not more than 10 .mu.m, orienting a mass of said finely comminuted mixture in a magnetic field, then forming said mass of mixture as compressed thereby obtaining a shaped article, sintering said shaped article in an inert atmosphere at a temperature in the range of 1,150.degree. C. to 1,230.degree. C. for a period in the range of 3 to 6 hours, subjecting the sintered shaped article to a solution treatment at a temperature in the range of 1,120.degree. C. to 1,210.degree. C. for a period in the range of 3 to 12 hours subsequently keeping the resultant shaped article at a temperature in the range of 750.degree. C. to 850.degree. C. for a period in the range of 4 to 12 hours, and thereafter aging the shaped article by cooling.

A method for the production of a permanent-magnet material, comprising the steps of mixing a powdered alloy of a composition represented by the formula:

• R(Co.sub.1-X-Y-.alpha. Fe.sub.X Cu.sub.Y M.sub..alpha.).sub.A
• and a powdered alloy of a composition represented by the formula:
• R(Co.sub.1-X-Y-.alpha.-.beta.,Fe.sub.X Cu.sub.Y M.sub..alpha. M'.sub..beta.).sub.A
• in a ratio falling in the range of 1:1 to 1,000:1, thereby producing a mixture of a composition represented by the formula:
• R(Co.sub.1-X-Y-.alpha.-.beta. Fe.sub.X Cu.sub.Y M.sub..alpha. M'.sub..beta.).sub.A
• (wherein, X, Y, .alpha., .beta., and A respectively represent the following numbers:
• 0.01.ltoreq.X, 0.02.ltoreq.Y.ltoreq.0.25, 0.001.ltoreq..alpha..ltoreq.0.15,
• 0.0001.ltoreq..beta..ltoreq.0.001, 6.0.ltoreq.A.ltoreq.8.3, and 2.beta..ltoreq..beta.',
• providing that th amount of Fe to be added should be less than 15% by weight, based on the total amount of the composition, and R, M, and M' respectively represent the following constituents:
• R:
• At least one element selected from the group of rare earth elements,
• M:
• At least one element selected from the group consisting of Ti, Zr, Hf, Nb, V, and Ta, and
• M':
• B or B+Si),
• forming said mixture in a magnetic field under pressure thereby obtaining a shaped article, and sintering said shaped article at a temperature 0.degree. C. to 40.degree. C. lower than the temperature of loss by melting (the temperature at which the article can not retain required shape because the amount of liquid phase thereof becomes more than certain level in the sintering step).