Process of producing alumina-titanium carbide ceramic body
AssigneeGeneral Electric Company
InventorsMinyoung Lee, Lawrence E. Szala, Marcus P. Borom
Life of this patent
Estimating the term…
Abstract
High-strength, fine-grain, multi-phase substantially crystalline sintered ceramic bodies are produced by a process comprising the steps of cold pressing, followed by sintering at a high temperature, of a mixture of different powdered ceramic materials containing non-inhibitory components and a source of inhibitory components that can chemically interact at elevated temperatures generate gases which hinder densification or form phases undesirable for sintering provided that there is also included in the mixture an amount of a source of a component co-reactive with the gases produced by the inhibitory components at elevated temperature to achieve efficient densification and retention of properties in the sintered body.
Claims15
In a process of making a multi-phase, substantially crystalline, sintered ceramic body, consisting essentially of
- (i) preparing a mixture consisting essentially of 40% to 80% by weight aluminum oxide powder and from about 20% by weight to about 60% by weight titanium carbide powder,
- (ii) consolidating said mixture under pressure to produce a pressed powder body;
- (iii) heating said body in an unconfined state to at least a sintering temperature;
- (iv) holding said body at sintering temperature for a period at least sufficiently long enough to achieve uniform temperature distribution throughout the body;
- and
- (v) recovering said sintered body, the improvement which consists essentially of including in said mixture a member selected from the group consisting of zirconium hydride, hafnium hydride, niobium hydride, tantalum hydride, titanium hydride, vanadium hydride and a mixture thereof, said member ranging from about 0.5% by weight to about 5% by weight of said mixture and being present in an amount sufficient to produce a sintered body having a minimum Rockwell A hardness of 91, said sintering temperature ranging from about 1650.degree. C. to about 1950.degree. C., said sintering being carrried out in a partial vacuum or atmosphere which has no significantly deleterious effect thereon.
A process for producing a sintered body having a minimum Rockwell A hardness of 91 which consists essentially of forming a mixture of aluminum oxide, titanium carbide and a metal hydride into a compact, said metal hydride being selected from the group consisting of zirconium hydride, hafnium hydride, niobium hydride, tantalum hydride, titanium hydride, vanadium hydride and mixture thereof, said metal hydride ranging from about 0.5% by weight to about 5% by weight of the total amount of said aluminum oxide and titanium carbide and being present in an amount sufficient to produce said sintered body, said titanium carbide ranging from about 20% by weight to about 60% by weight of the total amount of said aluminum oxide and titanium carbide, and sintering said compact in an unconfined state at a temperature ranging from about 1650.degree. C. to about 1950.degree. C., said sintering being carried out in a partial vacuum or atmosphere which has no significantly deleterious effect thereon.
A process for sintering an aluminum oxide-base powder to produce a sintered body having a minimum Rockwell-A hardness of 91 which consists essentially of forming said powder into a compact, said powder containing titanium carbide in an amount sufficient to impede densification of said compact with time at elevated temperature, said powder containing a metal hydride selected from the group consisting of zirconium hydride, hafnium hydride, niobium hydride, tantalum hydride, titanium hydride, vanadium hydride and a mixture thereof, said metal hydride ranging from about 0.5% by weight to about 5% by weight of the total amount of said aluminum oxide and titanium carbide powders and being present in an amount sufficient to enable production of said sintered body, and sintering said compact in an unconfined state at a temperature ranging from about 1650.degree. C. to about 1950.degree. C., said sintering being carried out in a partial vacuum or atmosphere which has no significantly deleterious effect thereon.
Dependencies are inferred from the claim text.